摘要
Thickness effects of thin La0.7Sr0.3MnO3 （LSMO） films on （LaAlOa）0.3（Sr2AlTaO6）0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function of thickness and differnt annealing conditions. Results reveal there could be more than one mechanism to induce vacancy-like defects. It was found that strain-induced defects mainly influence the S value of the in situ oxygenambience annealing LSMO thin films and the strain could vanish still faster along with the increase of thickness, and the oxygen-deficient induced defects mainly affect the S value of post-annealing LSMO films.