摘要
0.144（K0.5Bi0.5）TiO3-0.85（Na0.5Bi0.5）TiO3-0.006BaTiO3（KBT-NBT-BT） lead-free piezoelectric ceramics were prepared using a conventional solid state method.The influence of Sb2O3 doping on the crystal phase,surface microstructure and properties of the KBT-NBT-BT lead-free piezoelectric ceramics were investigated using X-ray diffraction（XRD）,scanning electron microscope（SEM） and other analytical methods.The results show that all compositions are of pure perovskite structure solid states.Sb2O3 doping does not influence the microstructure of KBT-NBT-BT lead-free piezoelectric ceramics obviously in the Sb2O3 doping range of 0.1-0.5 wt.%.Sb2O3 functions as a donor when doped small amount,while functions as a acceptor when doped large amount.The piezoelectric strain constant（d33） increases first and then decreases;the dielectric constant（ε33^T/ε0） and the dielectric loss（tanδ） decrease continuously when the amount of Sb2O3 dopant increases.When the doping amount of Sb2O3 is 0.1 wt.%,the KBT-NBT-BT piezoelectric ceramics with good comprehensive properties are obtained,whose d33,ε33^T/ε0 and tanδ are 147 pC/N,1510 and 4.2%,respectively.
0.144（K0.5Bi0.5）TiO3-0.85（Na0.5Bi0.5）TiO3-0.006BaTiO3（KBT-NBT-BT） lead-free piezoelectric ceramics were prepared using a conventional solid state method.The influence of Sb2O3 doping on the crystal phase,surface microstructure and properties of the KBT-NBT-BT lead-free piezoelectric ceramics were investigated using X-ray diffraction（XRD）,scanning electron microscope（SEM） and other analytical methods.The results show that all compositions are of pure perovskite structure solid states.Sb2O3 doping does not influence the microstructure of KBT-NBT-BT lead-free piezoelectric ceramics obviously in the Sb2O3 doping range of 0.1-0.5 wt.%.Sb2O3 functions as a donor when doped small amount,while functions as a acceptor when doped large amount.The piezoelectric strain constant（d33） increases first and then decreases;the dielectric constant（ε33^T/ε0） and the dielectric loss（tanδ） decrease continuously when the amount of Sb2O3 dopant increases.When the doping amount of Sb2O3 is 0.1 wt.%,the KBT-NBT-BT piezoelectric ceramics with good comprehensive properties are obtained,whose d33,ε33^T/ε0 and tanδ are 147 pC/N,1510 and 4.2%,respectively.