摘要
The direct decomposition of N2O was investigated over a series of magnesium cobaltite catalysts,MgxCo1-xCo2O4(0.0 ≤ x ≤ 1.0) ,which were prepared by the thermal decomposition of stoichiometric amounts of magnesium hydroxide and cobalt acetate. The thermal genesis of the different catalysts from their precursors was explored using thermogravimetric analysis,differential thermal analysis,and X-ray diffraction. Texture analysis was carried out using N2 adsorption at -196 °C. We found that all the catalysts that were calcined at 500 °C have a spinel structure. N2O decomposition activity was found to increase with an increase in the spinel structure's magnesium content. The influence of alkali cation promoters(Li,Na,K,and Cs) on the activity of the most active catalyst in the MgxCo1-xCo2O4 series,i.e. MgCo2O4,was also investigated. The sequence of the promotional effect was found to be: un-promoted < Li < Na < Cs < K-promoted catalyst. The reason for the increase in activity for the added alkali cations was electronic in nature. Additionally,the dependence of the activity on the K/Co ratio was also determined. The highest activity was obtained for the catalyst with a K/Co ratio of 0.05. A continuous decrease in activity was obtained for higher K/Co ratios. This decrease in activity was attributed to the elimination of mesoporosity in the catalysts with K/Co ratios > 0.05,based on N2 adsorption and scanning electron microscopy results.
The direct decomposition of N2O was investigated over a series of magnesium cobaltite catalysts,MgxCo1-xCo2O4（0.0 ≤ x ≤ 1.0） ,which were prepared by the thermal decomposition of stoichiometric amounts of magnesium hydroxide and cobalt acetate. The thermal genesis of the different catalysts from their precursors was explored using thermogravimetric analysis,differential thermal analysis,and X-ray diffraction. Texture analysis was carried out using N2 adsorption at –196 °C. We found that all the catalysts that were calcined at 500 °C have a spinel structure. N2O decomposition activity was found to increase with an increase in the spinel structure＇s magnesium content. The influence of alkali cation promoters（Li,Na,K,and Cs） on the activity of the most active catalyst in the MgxCo1-xCo2O4 series,i.e. MgCo2O4,was also investigated. The sequence of the promotional effect was found to be： un-promoted Li Na Cs K-promoted catalyst. The reason for the increase in activity for the added alkali cations was electronic in nature. Additionally,the dependence of the activity on the K/Co ratio was also determined. The highest activity was obtained for the catalyst with a K/Co ratio of 0.05. A continuous decrease in activity was obtained for higher K/Co ratios. This decrease in activity was attributed to the elimination of mesoporosity in the catalysts with K/Co ratios 0.05,based on N2 adsorption and scanning electron microscopy results.
出处
《催化学报》
SCIE
EI
CAS
CSCD
北大核心
2011年第2期264-272,共9页
基金
Supported by Assiut University