The deactivation of nickel catalysts used in Arak and Razi petrochemical complexes followed by catalyst regeneration was evalu-ated. The characterization of the different structures was made by powder X-ray diffraction(XRD),scanning electron microscopy(SEM),energy dispersive X-ray spectroscopy(EDS),transmission electron microscopy(TEM),and carbon & sulfur analyzer. The Ni particle size was estimated from XRD patterns and TEM graphs. The agglomeration of nickel particle and the poison by sulfur components were recognized as the main reasons in deactivation of Arak and Razi catalysts,respectively. The activity of the used catalysts before and after regeneration was measured on methane steam reforming at a CH4:H2O ratio of 1:3 at 850 oC. The regeneration processes for Arak and Razi samples were performed with CO2 as an oxidative atmosphere and steam as a regenerating agent,respectively. The results show that,(1) no residual sulfur components were on the regenerated Razi catalyst surface without changing the structure of the catalyst and the regenerated catalyst has gained 80% of its catalytic activity,and that(2) the nickel particle size of regenerated Arak specimen decreased remarkably as measured by Debye-Scherrer equation from XRD patterns. TEM images were in agreement with the XRD results and indicated a decrease in nickel particle size of regenerated catalyst. Additionally,in both regenerated catalysts all the coke on the surface of the support was eliminated after regeneration.
The deactivation of nickel catalysts used in Arak and Razi petrochemical complexes followed by catalyst regeneration was evalu-ated. The characterization of the different structures was made by powder X-ray diffraction（XRD）,scanning electron microscopy（SEM）,energy dispersive X-ray spectroscopy（EDS）,transmission electron microscopy（TEM）,and carbon sulfur analyzer. The Ni particle size was estimated from XRD patterns and TEM graphs. The agglomeration of nickel particle and the poison by sulfur components were recognized as the main reasons in deactivation of Arak and Razi catalysts,respectively. The activity of the used catalysts before and after regeneration was measured on methane steam reforming at a CH4：H2O ratio of 1：3 at 850 oC. The regeneration processes for Arak and Razi samples were performed with CO2 as an oxidative atmosphere and steam as a regenerating agent,respectively. The results show that,（1） no residual sulfur components were on the regenerated Razi catalyst surface without changing the structure of the catalyst and the regenerated catalyst has gained 80% of its catalytic activity,and that（2） the nickel particle size of regenerated Arak specimen decreased remarkably as measured by Debye-Scherrer equation from XRD patterns. TEM images were in agreement with the XRD results and indicated a decrease in nickel particle size of regenerated catalyst. Additionally,in both regenerated catalysts all the coke on the surface of the support was eliminated after regeneration.
出处
《催化学报》
SCIE
EI
CAS
CSCD
北大核心
2011年第2期273-279,共7页