磁性纳米纤维复合材料原位诱导体内成骨的研究(英文) 被引量:3

Enhancement of a magnetic nanofibrous composite scaffold for bone regeneration
下载PDF
导出
摘要 目的:研究一种新型顺磁性的纳米纤维复合支架γ-Fe2O3/nHAP/PDLLA在弱磁场下体内诱导新骨形成的功效。方法:纳米纤维复合材料支架通过电纺丝方法制成,支架内部的微观结构用扫描电镜(SEM)进行表征。将支架植入兔横突根部骨缺损处并在12周后处死动物,应用组织学方法研究支架在动物体内原位诱导新骨形成和胶原蛋白沉积的情况。结果:与对照的nHAP/PDLLA纳米纤维支架相比,磁性纳米纤维复合支架上有更多的Ⅰ型胶原沉积,新骨的生成量也明显增加。结论:磁性纳米纤维复合支架能够促进骨缺损部位的新骨生成,在引导骨组织再生与修复方面具有应用潜能。 Objective:To investigate the function of inducing bone regeneration of a novel paramagnetic nanofibrous composite scaffold of γ-Fe2O3/nHAP/PDLLAin vivounder a weak applied magnetic field.Methods: The scaffold was fabricated with the composite by electrospinning technique.The microstructure of the scaffold was characterized by scanning electron microscopy.The scaffold was implanted in defects at the root segment of the lumbar transverse process on a rabbit model.Bone tissue samples were collected after 12 weeks of implant surgery.New bone formation in the defects was assessed using histological analysis in reference to a control nanofibrous composite of nHAP/PDLLA.Deposition of typeⅠ collagen fibers were examined by Sirius red staining.Results: There was newbone formation observed in the scaffold.TypeⅠ collagen was deposited abundantly on the scaffold.Together all,the bone regeneration was enhanced obviously in comparison with that induced by control scaffold of nHAP/PDLLA.Conclusion: The scaffold of γ-FeO/nHAP/PDLLAenhanced osteogenesis under a weak static magnetic field,and exhibited promising potential for use in bone repair.
出处 《东南大学学报(医学版)》 CAS 2011年第1期1-6,共6页 Journal of Southeast University(Medical Science Edition)
基金 National Natural Science Foundation of China(30970710) Beijing Municipal Natural Science Foundation(2102046)
关键词 纳米纤维支架 γ-Fe2O3/nHAP/PDLLA复合材料 Ⅰ型胶原 骨再生 nanofibrous scaffold composite of γ-Fe2O3/nHAP/PDLLA typeⅠ collagen bone regeneration rabbits
  • 相关文献

参考文献16

  • 1KOSTOPOULOS V,VELLIOS L,LAMBIRIS E,et al.Comparative study of callus performance achieved by rigid and sliding plate osteosythesis based upon dynamic mechnical analysis[J].J Med Eng,1994,18(2):61-66.
  • 2MOLLY M S.Biomaterials for bone tissue engineering[J].Mater Today,2008,11(5):18-25.
  • 3KIM S S,PARK M S,KIM B S,et al.Poly (lactide-co-glycolide)/hydroxyapatite composite scaffolds for bone tissue engineering[J].Biomaterials,2006,27(8):1399-1409.
  • 4PEK Y S,GAO S J,YING J Y,et al.Porous collagen-apatite nanocomposite foams as bone regeneration scaffolds[J].Biomaterials,2008,29(32):4300-4305.
  • 5WANG H N,LI Y B,CHENG L,et al.Biocompatibility and osteogenesis of biomimetic nano-hydroxyapatite /Poly-amide composite scaffolds for bone tissue regeneration[J].Biomaterials,2007,28(22):3338-3348.
  • 6LIU Y,LU Y,ZHANG B X,et al.Segmental bone regeneration using an rhBMP-2-loaded gelatin /nanohydroxyapatite /fibrin scaffold in a rabbit model[J].Biomaterials,2009,30(31):6276-6285.
  • 7PURICELLI E,DUTRA N B,PONZONI D.Histological evaluation of the influence of magnetic field application in autogenous bone grafts in rats[J].Head Face Med,2009,5:1.
  • 8KOTANI H,KAWAGUCHI H,HOSHI K,et al.Strong static magnetic field stimulates bone formation to a definite orientation in vitro and in vivo[J].J Biomed Mater Res,2002,17(10):1814-1821.
  • 9YAN Q C,TOMITA N,IKADA Y.Effects of static magnetic field on bone formation of rat femurs[J].Med Eng Phys,1998,20(6):397-402.
  • 10ZHANG S,ZHANG Y,GU N,et al.Preparation of anti-sperm protein 17 immunomagnetic nanoparticles for targeting cell[J].J Nanosci Nanotechnol,2007,8(1):1-6.

同被引文献90

引证文献3

二级引证文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部