摘要
为了制备Ni基非晶涂层,采用激光熔覆方法在45~#钢基体上制备Ni_(60.5)Zr_(19.63)Nb_(18.07)Al_(1.8)非晶复合涂层,分析了涂层显微组织及物相,测得了表征力学及耐蚀性能的实验数据。结果表明,涂层中存在大量呈树枝状和胞状的晶体相,由X射线衍射分析可知,涂层中出现了非晶及NiZr_2,Ni_5Nb,Al_2O_3和Fe-Ni金属间化合物等物相;当功率为3600W时,涂层中白色非晶相含量最多,且组织最为细小;功率为3000W时,涂层最高硬度在最表面,达到2399.9HK,表面耐磨失重为0.5921mg·mm^(-2);涂层耐蚀性能在功率为3600W时最佳,致钝电流密度最小为3.05mA/m^2,钝化区间最宽为1170mV。由新判据设计的Ni_(60.5)Zr_(19.63)Nb_(18.07)Al_(1.8)成分具有较强非晶形成能力。
In order to prepare Ni-based amorphous coatings,Ni60.5Zr19.63Nb18.07Al1.8 amorphous composite coating was prepared on 45# steel substrate by means of laser cladding. Then the microstructure and phase of the coating were analyzed and the parameters characterizing the mechanical and corrosion resistance were measured. The results show that a great deal of dendritic and cystiform crtstal phases exist in the coating. X-ray diffraction analysis reveals that amorphous, intermetallic compound such as Ni60.5Zr19.63Nb18.07Al1.8 and Fe-Ni, and some other phases present in the coating. Content of white amorphous phase is up to maximum at the power of 3600W, and microstructure is most fine; hardness reaches maximum at the power of 3000W and can be up to 2399.9HK at topmost surface, while surface wear weight loss is 0. 5921mg ·mm-2 ; coating corrosion resistance is the best at the power of 3600W. The minimum obtuse current density is 3.05mA/m2 , and passive potential widest range is 1170mV; Ni60.5Zr19.63Nb18.07Al1.8 designed according to the new criterion has strong glass forming ability.
出处
《激光技术》
CAS
CSCD
北大核心
2011年第2期185-188,共4页
Laser Technology
基金
辽宁省教育厅高等学校科研计划资助项目(2008297)
关键词
激光技术
激光熔覆
非晶
显微组织
性能
laser technique
laser cladding
amorphous
microstructure
performance