采用固相法制备了10 at%Yb^(3+):GdGaGe_2O_7多晶粉体,通过X射线粉末衍射用Rietveld全谱拟合给出了其空间群为P2_1/c,晶格常数a、b、c和β,Gd/Yb和Ga的原子坐标,以及Ge1、Ge2、O1~O7的原子坐标。通过吸收谱、激发谱、光致发光谱和Raman光谱确定Yb^(3+)的晶场能级分裂,1003 nm发光在低温(8 K)和室温(300 K)时上能级荧光寿命为0.493 ms和0.774 ms。在室温下测量荧光寿命变长主要由再吸收引起。Yb^(3+):GdGaGe_2O_7的吸收和发射光谱均很宽,荧光寿命长,是潜在的全固态激光工作物质。
10 at%Yb^3+:GdGaGe2O7 powders were prepared by solid state reaction method,and its structure was determined by the Rietveld refinement to the X-ray powder diffraction.Its space group is P2_1/c,lattice parameters of a,b,c,βand the atomic coordinates of Gd/Yb,Ga,Gel,Ge2 and O1~O7 were obtained. The crystal field splitting of Yb^3+ in GdGaGe_2O_7 was determined according to its absorption,excitation, emission and Raman spectra.The lifetime of 1003 nm emission is 0.493 ms at low temperature(8 K) and 0.774 ms at room temperature(300 K),and the obtained decay-time is longer at room temperature which is caused by its re-absorption.The emission and absorption spectra of Yb^3+:GdGaGe2O7 are relatively wide, the luminescence decay time is long,and it is a potential all-solid-state-laser medium.
出处
《量子电子学报》
CAS
CSCD
北大核心
2011年第2期234-240,共7页
Chinese Journal of Quantum Electronics
基金
国家自然科学基金(90922003
50772112
50872135
50932005)
中科院知识创新项目(YYYJ-1002)资助课题