摘要
A novel UV-curable prepolymer hexanediol diglycidyl ether diacrylate （HDGEA） was synthesized by utilizing hexanediol diglycidyl ether （HDGE） and acrylic acid （AA） as starting materials, N, N-dimethylbenzylamine as catalyst and p-hydroxyanisole as inhibitor. The optimal synthetic conditions were that the concentration of N, N-dimethylbenzylamine was 0.80 wt% of reactants, the concentration of p-hydroxyanisole was 0.3 wt% of reactants, the reaction temperature was 90-110 ℃, and the molar ratio of HDGE to AA was 1︰2.2. Meanwhile, 1-hydroxycyclohexyl phenyl ketone of a UV-curing initiator was added to the synthesized HDGEA to prepare a kind of UV-curing coating. The mechanical properties of the UV-cured films were determined, giving 31.87 MPa of tensile strength, 871.88 MPa of Young＇s modulus and 6.77% of elongation at tear.
A novel UV-curable prepolymer hexanediol diglycidyl ether diacrylate （HDGEA） was synthesized by utilizing hexanediol diglycidyl ether （HDGE） and acrylic acid （AA） as starting materials, N, N-dimethylbenzylamine as catalyst and p-hydroxyanisole as inhibitor. The optimal synthetic conditions were that the concentration of N, N-dimethylbenzylamine was 0.80 wt% of reactants, the concentration of p-hydroxyanisole was 0.3 wt% of reactants, the reaction temperature was 90-110 ℃, and the molar ratio of HDGE to AA was 1︰2.2. Meanwhile, 1-hydroxycyclohexyl phenyl ketone of a UV-curing initiator was added to the synthesized HDGEA to prepare a kind of UV-curing coating. The mechanical properties of the UV-cured films were determined, giving 31.87 MPa of tensile strength, 871.88 MPa of Young＇s modulus and 6.77% of elongation at tear.
基金
Funded by the Natural Science Foundation of Jiangxi Province (No.2008GZC0021)
the National "863" Hi-tech Foundation of China (No.2002AA6Z3083)