摘要
The effects of lanthanum-praseodymium-cerium mischmetal （LPC） on the microstructure and mechanical properties of Mg-Al alloy were investigated. With the addition of LPC, an additional rod-like Al11La3 phase was deposited in the alloy. LPC greatly improves the tensile strength of cast Mg-Al alloys but negatively affects the elongation of cast alloys above 473 K. Cast alloys are strengthened by both precipitation strengthening and dispersion strengthening at ambient temperature. When the temperature exceeds 473 K, only the dispersion operates as a strengthening mechanism.
The effects of lanthanum-praseodymium-cerium mischmetal （LPC） on the microstructure and mechanical properties of Mg-Al alloy were investigated. With the addition of LPC, an additional rod-like Al11La3 phase was deposited in the alloy. LPC greatly improves the tensile strength of cast Mg-Al alloys but negatively affects the elongation of cast alloys above 473 K. Cast alloys are strengthened by both precipitation strengthening and dispersion strengthening at ambient temperature. When the temperature exceeds 473 K, only the dispersion operates as a strengthening mechanism.