A series of poly(aryl ether ketone ether ketone ketone)containing meta\|phenyl link were
prepared by low temperature solution polycondensation of 4,4\|diphenoxybenzophenone
(DPBP),terephthaloyl chloride(TPC) and isophthaloyl chloride(IPC) in 1 ,2\|dichloroethane and in
the presence of AlCl\-3 and NMP.DSC,TGA and wide\|angle X\|ray scattering,etc.were used to
study the general properties of the polymers.With the increase of IPC content,the T\-g and
crystallinity decreased,the T\-m decreased at first,and then disappeared.But for all meta\|linked
polymer,T\-m appeared once more.And this kind of polymer exhibited good chemical resistance.
The structures of crystal polymer have a close resemblance to that of poly(ether ketone ketone).
The cell dimensions of copolymer containing 30% IPC were calculated to be a=0\^7781
nm,b=0\^6022 nm,and c=1\^012 nm. The kinetics of thermal degradation of it was also studied
by dynamic thermogravimetry in nitrogen.The resutls calculated from the kinetic models based
on rand om initiation followed by rapid disproportionation and termination were in good
agreement with the experimental data.The overall activation energy for degradation was found
to be 440\^1 kJmol\+\{-1\}.\=
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
1999年第4期490-493,共4页
Acta Polymerica Sinica
基金
国家"863"计划项目
江西省自然科学基金
关键词
PEKEKK
合成
聚醚酮醚酮酮
间苯基
Poly(aryl ether ketone ether ketone ketone),Meta\|phenyl
link,Melting point,Crystallinity,Dynamic thermogravimetry