LiMn2O4/graphite batteries using LiF additive were fabricated and their electrochemical performance including discharge, cycling and storage performances were tested and compared with LiF-free LiMnEO4/graphite batteries. The LiMnEO4/graphite battery with LiF added shows better capacity (107.5 mAh/g), cycling performance (capacity retention ratio of 93% after 100 cycles), and capacity recovery ratio (98.1%) than the LiF-free battery. The improvement in electrochemical performance of the LiF-added LiMnEO4/graphite battery was due to the fact that LiF can restrain the dissolution of Mn from the spinel LiMn2O4 cathode into the electrolyte, leading to a smaller resistance and polariza- tion.
LiMn2O4/graphite batteries using LiF additive were fabricated and their electrochemical performance including discharge, cycling and storage performances were tested and compared with LiF-free LiMnEO4/graphite batteries. The LiMnEO4/graphite battery with LiF added shows better capacity (107.5 mAh/g), cycling performance (capacity retention ratio of 93% after 100 cycles), and capacity recovery ratio (98.1%) than the LiF-free battery. The improvement in electrochemical performance of the LiF-added LiMnEO4/graphite battery was due to the fact that LiF can restrain the dissolution of Mn from the spinel LiMn2O4 cathode into the electrolyte, leading to a smaller resistance and polariza- tion.
基金
supported by the Advanced Person Fund of Jiangsu University (No. 10JDG041)
the Major State Basic Research Development Program of China(No. 2007CB613607)