摘要
Vanadium films were prepared on zinc surfaces by using a solution containing vanadate. Corrosion protection properties of vanadium-treated （V-treated）, chromium-treated （Cr-treated）, and untreated zinc surfaces in contact with a 3.5 wt.% NaC1 solution were studied using potentiodynamic polarization, electrochemical impedance spectroscopy （EIS）, and neutral salt spray （NSS） tests. According to these results, the V-treated layer significantly improved the corrosion resistance of zinc surfaces. In comparison with the Cr-treated layer, the V-treated layer exhibited a better corrosion resistance. The composition of the V-treated layer was studied using X-ray photoelectron spectroscopy （XPS）. XPS measurements indicated that the vanadium layer formed on zinc surfaces and the vanadium-rich coating was a hydrated oxide with a composition of V2O5, VO2, and its hydrates such as V2O5.nH2O and VO（OH）2.
Vanadium films were prepared on zinc surfaces by using a solution containing vanadate. Corrosion protection properties of vanadium-treated （V-treated）, chromium-treated （Cr-treated）, and untreated zinc surfaces in contact with a 3.5 wt.% NaC1 solution were studied using potentiodynamic polarization, electrochemical impedance spectroscopy （EIS）, and neutral salt spray （NSS） tests. According to these results, the V-treated layer significantly improved the corrosion resistance of zinc surfaces. In comparison with the Cr-treated layer, the V-treated layer exhibited a better corrosion resistance. The composition of the V-treated layer was studied using X-ray photoelectron spectroscopy （XPS）. XPS measurements indicated that the vanadium layer formed on zinc surfaces and the vanadium-rich coating was a hydrated oxide with a composition of V2O5, VO2, and its hydrates such as V2O5.nH2O and VO（OH）2.