摘要
Zinc oxide （ZnO） thin films were deposited on sapphire （0001） substrates at room temperature by radiofrequency （RF） magnetron sputtering at oxygen gas contents of 0%, 25%, 50% and 75%, respectively. The influence of oxygen gas content on the structural and optical properties of ZnO thin films was studied by a surface profile measuring system, X-ray diffraction analysis, atomic force microscopy, and UV spectro- photometry. It is found that the size of ZnO crystalline grains increases first and then decreases with the increase of oxygen gas content, and the maximum grain size locates at the 25% oxygen gas content. The crystalline quality and average optical transmittance （〉90%） in the visi- ble-light region of the ZnO film prepared at an oxygen gas content of 25% are better than those of ZnO films at the other contents. The obtained results can be attributed to the resputtefing by energetic oxygen anions in the growing process.
Zinc oxide （ZnO） thin films were deposited on sapphire （0001） substrates at room temperature by radiofrequency （RF） magnetron sputtering at oxygen gas contents of 0%, 25%, 50% and 75%, respectively. The influence of oxygen gas content on the structural and optical properties of ZnO thin films was studied by a surface profile measuring system, X-ray diffraction analysis, atomic force microscopy, and UV spectro- photometry. It is found that the size of ZnO crystalline grains increases first and then decreases with the increase of oxygen gas content, and the maximum grain size locates at the 25% oxygen gas content. The crystalline quality and average optical transmittance （〉90%） in the visi- ble-light region of the ZnO film prepared at an oxygen gas content of 25% are better than those of ZnO films at the other contents. The obtained results can be attributed to the resputtefing by energetic oxygen anions in the growing process.
基金
supported by the National Natural Science Foundation of China (Nos. 60876055 and11074063)
the Natural Science foundation of Hebei Province,China (Nos. E2008000620 and E2009000207)
the Specialized Research Fund for the Doctoral Program of Higher Education of China (No. 20091301110002)
the Key Basic Research Program of Hebei Provincial Applied Basic Research Plan (No. 10963525D)