The phase relation, microstructure, Curie temperatures, hysteresis, and magnetocaloric effects of LaFex＊11.6Si1.4 （x=0.96, 0.98, 1.0, and 1.02） compounds prepared by arc-melting and then annealed at 1423 K （1.5 h）＋1523 K （4.5 h） were investigated. The main phase was NaZn13-type phase, the impurity phases included a small amount of α-Fe and LaFeSi phase in four samples. The crystal cell parameters of 1：13 phase increased from 1.1433（5） to 1.1454（4） nm with x increasing from 0.96 to 1.02, respectively. All samples kept the typical first-order magnetic transition. The increase of Fe strengthened IEM behavior, and led to the remarkable enhancement of MCE effect and negative slopes in Arrott plots around TC. The maximum ΔSM （T, H） under a low magnetic field （0–2 T） was 15.3, 16.8, 17.9, and 24.7 J/kg K with increasing of Fe content from x=0.96 to 1.02, respectively.
The phase relation, microstructure, Curie temperatures, hysteresis, and magnetocaloric effects of LaFex＊11.6Si1.4 （x=0.96, 0.98, 1.0, and 1.02） compounds prepared by arc-melting and then annealed at 1423 K （1.5 h）＋1523 K （4.5 h） were investigated. The main phase was NaZn13-type phase, the impurity phases included a small amount of α-Fe and LaFeSi phase in four samples. The crystal cell parameters of 1：13 phase increased from 1.1433（5） to 1.1454（4） nm with x increasing from 0.96 to 1.02, respectively. All samples kept the typical first-order magnetic transition. The increase of Fe strengthened IEM behavior, and led to the remarkable enhancement of MCE effect and negative slopes in Arrott plots around TC. The maximum ΔSM （T, H） under a low magnetic field （0–2 T） was 15.3, 16.8, 17.9, and 24.7 J/kg K with increasing of Fe content from x=0.96 to 1.02, respectively.
基金
supported by the Key Project of National Natural Science Foundation of China (50731007)
the National High Technology Research and Development Program of China (2007AA03Z440)