摘要
The activated carbon(AC)was prepared from Solidago Canadensis(SC),an alien invasive plant.The plant was firstly carbonized under nitrogen at 400 ℃ for 90 min in an electrical furnace,and then the carbonized product was activated with KOH through microwave radiation.Effects of KOH/C ratio,microwave power,microwave radiation time on the adsorption capacities and yield of AC were evaluated.It indicated that the optimum conditions were KOH/C ratio 2 g/g,microwave power 700 W,and microwave radiation time 6 min.The carbonation process of SC was analyzed by thermogravimetry(TG).The pore structural parameters and surface functional groups of the AC were characterized by nitrogen adsorption-desorption and Fourier Transformed Infrared Spectroscopy(FTIR),respectively.The activation yield,the surface area,the average pore size,and the average micropore size of AC prepared from optimum conditions were 53.75%,1 888 m2/g,0.567 nm,and 0.488 nm,respectively.The adsorption amounts of AC were 302.4 mg/g for methylene blue and 1 470.27 mg/g for iodine.
The activated carbon（AC）was prepared from Solidago Canadensis（SC）,an alien invasive plant.The plant was firstly carbonized under nitrogen at 400 ℃ for 90 min in an electrical furnace,and then the carbonized product was activated with KOH through microwave radiation.Effects of KOH/C ratio,microwave power,microwave radiation time on the adsorption capacities and yield of AC were evaluated.It indicated that the optimum conditions were KOH/C ratio 2 g/g,microwave power 700 W,and microwave radiation time 6 min.The carbonation process of SC was analyzed by thermogravimetry（TG）.The pore structural parameters and surface functional groups of the AC were characterized by nitrogen adsorption-desorption and Fourier Transformed Infrared Spectroscopy（FTIR）,respectively.The activation yield,the surface area,the average pore size,and the average micropore size of AC prepared from optimum conditions were 53.75%,1 888 m2/g,0.567 nm,and 0.488 nm,respectively.The adsorption amounts of AC were 302.4 mg/g for methylene blue and 1 470.27 mg/g for iodine.
基金
Shanghai Leading Academic Discipline Project,China(No.B604)