The layered LiNi0.6Co0.2-xMn0.2MgxO2 （x=0.00,0.03,0.05,0.07） cathode materials were prepared by a co-precipitation method.The properties of the Mg-doped LiNi0.6Co0.2Mn0.2O2 were investigated by X-ray diffraction （XRD）,scanning electron microscopy （SEM）,and electrochemical measurements.XRD studies showed that the Mg-doped LiNi0.6Co0.2Mn0.2O2 had the same layered structure as the undoped LiNi0.6Co0.2Mn0.2O2.The SEM images exhibited that the particle size of Mg-doped LiNi0.6Co0.2Mn0.2O2 was finer than that of the undoped LiNi0.6Co0.2 Mn0.2O2 and that the smallest particle size is only about 1μm.The Mg-doped LiNi0.6Co0.2Mn0.2O2 samples were investigated on the Li extraction/insertion performances through charge/discharge,cyclic voltammogram （CV）,and electrochemical impedance spectra（EIS）.The optimal doping content of Mg was that x= 0.03 in the LiNi0.6Co0.2-xMn0.2MgxO2 samples to achieve high discharge capacity and good cyclic stability.The electrode reaction reversibility and electronic conductivity was enhanced,and the charge transfer resistance was decreased through Mg-doping.The improved electrochemical performances of the Mg-doped LiNi0.6Co0.2Mn0.2O2 cathode materials are attributed to the addition of Mg 2＋ ion by stabilizing the layer structure.
The layered LiNi0.6Co0.2-xMn0.2MgxO2 （x=0.00,0.03,0.05,0.07） cathode materials were prepared by a co-precipitation method.The properties of the Mg-doped LiNi0.6Co0.2Mn0.2O2 were investigated by X-ray diffraction （XRD）,scanning electron microscopy （SEM）,and electrochemical measurements.XRD studies showed that the Mg-doped LiNi0.6Co0.2Mn0.2O2 had the same layered structure as the undoped LiNi0.6Co0.2Mn0.2O2.The SEM images exhibited that the particle size of Mg-doped LiNi0.6Co0.2Mn0.2O2 was finer than that of the undoped LiNi0.6Co0.2 Mn0.2O2 and that the smallest particle size is only about 1μm.The Mg-doped LiNi0.6Co0.2Mn0.2O2 samples were investigated on the Li extraction/insertion performances through charge/discharge,cyclic voltammogram （CV）,and electrochemical impedance spectra（EIS）.The optimal doping content of Mg was that x= 0.03 in the LiNi0.6Co0.2-xMn0.2MgxO2 samples to achieve high discharge capacity and good cyclic stability.The electrode reaction reversibility and electronic conductivity was enhanced,and the charge transfer resistance was decreased through Mg-doping.The improved electrochemical performances of the Mg-doped LiNi0.6Co0.2Mn0.2O2 cathode materials are attributed to the addition of Mg 2＋ ion by stabilizing the layer structure.
基金
Funded by the Scientific Research Fund of Hunan Education Department(10C0294)