Passivation process of X80 pipeline steel in bicarbonate solutions 被引量:8

Passivation process of X80 pipeline steel in bicarbonate solutions
下载PDF
导出
摘要 The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electro-chemical impedance spectroscopy (DEIS), and Mott-Schottky measurements. The results show that the shape of polarization curves changes with concentration. The critical 'passive' concentration is 0.009 mol/L for X80 pipeline steel in bicarbonate solutions. No anodic current peak exists in solutions when the concentration is lower than 0.009 mol/L, whereas there are one and two anodic current peaks when the concentration ranges from 0.009 to 0.05 mol/L and is higher than 0.1 mol/L, respectively. DEIS measurements show that there exist active dissolution range, transition range, pre-passive range, passive layer formation range, passive range, and trans-passive range for X80 pipeline steel in the 0.1 mol/L solutions. The results of DEIS measurements are in complete agreement with the potentiodynamic diagram. An equivalent circuit containing three sub-layers is used to explain the Nyquist plots in the passive range. Analyses are well made for explaining the corresponding fitted capacitance and impedance. The Mott-Schottky plots show that the passive film of X80 pipeline steel is an n-type semiconductor, and capacitance measurements are in good accordance with the results of DEIS experiment. The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electro-chemical impedance spectroscopy (DEIS), and Mott-Schottky measurements. The results show that the shape of polarization curves changes with concentration. The critical 'passive' concentration is 0.009 mol/L for X80 pipeline steel in bicarbonate solutions. No anodic current peak exists in solutions when the concentration is lower than 0.009 mol/L, whereas there are one and two anodic current peaks when the concentration ranges from 0.009 to 0.05 mol/L and is higher than 0.1 mol/L, respectively. DEIS measurements show that there exist active dissolution range, transition range, pre-passive range, passive layer formation range, passive range, and trans-passive range for X80 pipeline steel in the 0.1 mol/L solutions. The results of DEIS measurements are in complete agreement with the potentiodynamic diagram. An equivalent circuit containing three sub-layers is used to explain the Nyquist plots in the passive range. Analyses are well made for explaining the corresponding fitted capacitance and impedance. The Mott-Schottky plots show that the passive film of X80 pipeline steel is an n-type semiconductor, and capacitance measurements are in good accordance with the results of DEIS experiment.
出处 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2011年第2期178-184,共7页 矿物冶金与材料学报(英文版)
基金 supported by the National Science and Technology Infrastructure Platforms Construction Projects (No.2005DKA10400)
关键词 pipeline steel bicarbonate solutions PASSIVATION potentiodynamic polarization electrochemical impedance spectroscopy pipeline steel bicarbonate solutions passivation potentiodynamic polarization electrochemical impedance spectroscopy
  • 相关文献

参考文献3

二级参考文献12

  • 1L.J.Zhang,Z.Zhang,F.H.Cao,J.Q.Zhang,J.M.Wang,C.N.Cao.STUDY OF THE X70 PIPELINE STEEL CORRODING IN 3.0wt% NaCl SOLUTION USING ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY TECHNIQUE[J].Acta Metallurgica Sinica(English Letters),2004,17(6):907-911. 被引量:11
  • 2Cheng Y F, Luo J L. Electronic structure and pitting susceptibility of passive film on carbon steel. Electrochim Acta, 1999, 44(17): 2947
  • 3Macdonald D D. Review of mechanistic analysis by electrochemical impedance spectroscopy. Electrochim Acta, 1990, 35 (10) : 1509
  • 4Macdonald D D. The point defect model for the passive state. J Electrochem Soc, 1992, 139(12): 3434
  • 5Macdonald D D, Macdonald M U. Theory of steady-state passive films. J Electrochem Soc, 1990, 137(8): 2395
  • 6Pagitsas M, Diamantpoulou A, Sazou D. A point defect model for the general and pitting corrosion on iron oxide electrolyte interface deduced from current oscillations. Chaos Solitons Fractals, 2003, 17(2/3): 263
  • 7Pagitsas M, Diamampoulou A, Sazou D. Distinction between general and pitting corrosion based on the nonlinear dynamical response of passive iron surfaces perturbed chemically by halides. Electrochem Commun, 2001, 3(7): 330
  • 8Krishnamurthy B, White R E, Ploehn H J. Simplified point defect model for growth of anodic passive films on iron. Electrochim Acta, 2002, 47(20): 3375
  • 9Davenport A J, Oblonsky L J, Ryan M P, et al. The structure of the passive film that forms on iron in aqueous environments. J Electrochem Soc, 2000, 147(6): 2162
  • 10Bojinov M, Laitinen T, Makela K, et al. Conduction mechanism of the passive film on iron based on contact electric impedance and resistance measurements. J Electrochem Soc, 2001, 148 ( 6 ) : B243

共引文献48

同被引文献76

引证文献8

二级引证文献27

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部