Promoter MgO on 10% CeO2/Al2O3 oxygen carrier was investigated for direct partial oxidation of methane to syngas in molten salt. The MgO content of 0.5%, 1%, 2%, 3% and 4% on the 10%CeO2/Al2O3 oxygen carriers in experiments were prepared at the temperature of 750℃, respectively. The methane conversion, H2 and CO selectivity was measured on these prepared oxygen carriers at different reaction temperature. The results showed that the 3% MgO on 10%CeO2/Al2O3 had the best activity, and the CH4 conversion and CO selectivity reached 92.58% and 87.64% at 875℃, respectively. The effect of different calcination temperature on 3% MgO as promoter on 10% CeO2/Al2O3 oxygen carrier was investigated. The results of BET indicated that oxygen carrier had the largest surface area at 750℃. When the calcined temperature was too high there would be a negative effect on oxygen carrier activity.
基金
Acknowledgments： The work was supported by the National Nature Science Foundation of China （No. 50574046, 50164002） and National Natural Science Foundation of Major Research Projects （No. 90610035）, Natural Science Foundation of Yunnan Province （No. 2004E0058Q）, High School Doctoral Subject Special Science and Research Foundation of Ministry of Education （No. 20040674005）.