摘要
Microspheres coated with a perfectly conductive surface have many advantages in the applications of biosensors and micro-electromechanical systems. Polystyrene microspheres with the diameter of 10 μm were coated with a 50 nmthick gold layer using an electroless gold plating approach. Dielectrophoresis （DEP） for bare microspheres and shelled microspheres was theoretically analysed and the real part of the Clausius Mossotti factor was calculated for the two kinds of microspheres. The experiments on the dielectrophoretic characterisation of the uncoated polystyrene microspheres and gold coated polystyrene microspheres （GCPMs） were carried out. Experimental results showed that the gold coated polystyrene microspheres were only acted by a positive dielectrophoretic force when the frequency was below 40M Hz, while the uncoated polystyrene microspheres were governed by a negative dielectrophoretic force in this frequency range. The gold coated polystyrene microspheres were exploited to form the rnicrowire automatically according to their stable dielectrophoretic and electric characterisations.
Microspheres coated with a perfectly conductive surface have many advantages in the applications of biosensors and micro-electromechanical systems. Polystyrene microspheres with the diameter of 10 μm were coated with a 50 nmthick gold layer using an electroless gold plating approach. Dielectrophoresis （DEP） for bare microspheres and shelled microspheres was theoretically analysed and the real part of the Clausius Mossotti factor was calculated for the two kinds of microspheres. The experiments on the dielectrophoretic characterisation of the uncoated polystyrene microspheres and gold coated polystyrene microspheres （GCPMs） were carried out. Experimental results showed that the gold coated polystyrene microspheres were only acted by a positive dielectrophoretic force when the frequency was below 40M Hz, while the uncoated polystyrene microspheres were governed by a negative dielectrophoretic force in this frequency range. The gold coated polystyrene microspheres were exploited to form the rnicrowire automatically according to their stable dielectrophoretic and electric characterisations.
基金
Project supported by the National Natural Science Foundation of China (Grant No. 51075087)
the State Key Laboratory of Fluid Power Transmission and Control,ZheJiang University of China (Grnat No. GZKF-201004)
the China Scholarship Council(Grant No. 2009612129)