摘要
A novel type of crosslinkable poly（aryl ether sulfone）（PAES） bearing an allyl pendant（PES-OAllyl） was synthesized by a grafting reaction of hydrophenyl-containing PAES（PES-OH） and allyl bromide. PES-OH was prepared by a demethylation reaction of a methoxyphenylated PAES（PES-OCH3） in the presence of pyridine/hydrochlo- ride. The PES-OCH3 was synthesized by an aromatic nucleophilic substitution of bis（4-chlorophenyl）sulfone and （p-methoxy）phenylhydroquinone. Both DSC and solubility investigation were used to study the crosslinking behavior of PES-OAllyl. After heat treatment, the glass transition temperature（Tg） value of PES-OAllyl sharply increased from 165 ℃ to 227 ℃. Meanwhile, PES-OAllyl changed from a soluble polymer to an insoluble thermoset. In addition, TGA（thermogravimetric analysis） result suggests that the thermal stability of the crosslinked product was improved. All the data prove that the crosslinked PES-OAllyl could be a potential solvent-resistance high-performance material.
A novel type of crosslinkable poly（aryl ether sulfone）（PAES） bearing an allyl pendant（PES-OAllyl） was synthesized by a grafting reaction of hydrophenyl-containing PAES（PES-OH） and allyl bromide. PES-OH was prepared by a demethylation reaction of a methoxyphenylated PAES（PES-OCH3） in the presence of pyridine/hydrochlo- ride. The PES-OCH3 was synthesized by an aromatic nucleophilic substitution of bis（4-chlorophenyl）sulfone and （p-methoxy）phenylhydroquinone. Both DSC and solubility investigation were used to study the crosslinking behavior of PES-OAllyl. After heat treatment, the glass transition temperature（Tg） value of PES-OAllyl sharply increased from 165 ℃ to 227 ℃. Meanwhile, PES-OAllyl changed from a soluble polymer to an insoluble thermoset. In addition, TGA（thermogravimetric analysis） result suggests that the thermal stability of the crosslinked product was improved. All the data prove that the crosslinked PES-OAllyl could be a potential solvent-resistance high-performance material.
基金
Supported by the National Natural Science Foundation of China(No.50973040)
the Science and Technology Development Plan of Jilin Province, China(No.20090322)