Simulation of Static Recrystallization Behavior of 58SiMn Steel

Simulation of Static Recrystallization Behavior of 58SiMn Steel
下载PDF
导出
摘要 58SiMn steel can be used as a kind of material for projectile-like barrel parts.During producing barrel parts,the microstructure of the barrel parts will be changed due to its hot deformation at certain high temperature,which resulted in the variety of the part's mechanical properties.It is necessary to optimize the parameters for recrystallization process by prediction and simulation.The double-pass hot compression tests were conducted using Gleeble 1500 System at different deformation temperature,strain rate and pre-strain.Effect of pre-strain,deformation temperature on the curve of stress-strain has been analyzed.The static recrystallization fraction of double-pass hot deformation was computed and analyzed using compensation test.The actual grain size was measured by metallographic method using oxidation process,which overcomes the difficulty in revealing grain size of 58SiMn steel.The oxidation process was the method of heating the martensite in very fast speed and use of its microstructure inherent characteristic and regarding the size of austenite grain as the maximum of martensite plate.Using regression of the experimental data,the mathematical model of static recrystallization is set up.The average grain size of 58SiMn steel during hot deformation was calculated by deform-3D software and verified by experiment.The results show that the rate of static recrystallization was in direct proportional to the pre-strain of the steel.The grain size decreased with the increase of holding time at low deformation temperature 1 173 K and pre-strain 0.10.The mathematical model proposed could be used for predicting the static recrystallization behaviors of 58SiMn steel. 58SiMn steel can be used as a kind of material for projectile-like barrel parts.During producing barrel parts,the microstructure of the barrel parts will be changed due to its hot deformation at certain high temperature,which resulted in the variety of the part's mechanical properties.It is necessary to optimize the parameters for recrystallization process by prediction and simulation.The double-pass hot compression tests were conducted using Gleeble 1500 System at different deformation temperature,strain rate and pre-strain.Effect of pre-strain,deformation temperature on the curve of stress-strain has been analyzed.The static recrystallization fraction of double-pass hot deformation was computed and analyzed using compensation test.The actual grain size was measured by metallographic method using oxidation process,which overcomes the difficulty in revealing grain size of 58SiMn steel.The oxidation process was the method of heating the martensite in very fast speed and use of its microstructure inherent characteristic and regarding the size of austenite grain as the maximum of martensite plate.Using regression of the experimental data,the mathematical model of static recrystallization is set up.The average grain size of 58SiMn steel during hot deformation was calculated by deform-3D software and verified by experiment.The results show that the rate of static recrystallization was in direct proportional to the pre-strain of the steel.The grain size decreased with the increase of holding time at low deformation temperature 1 173 K and pre-strain 0.10.The mathematical model proposed could be used for predicting the static recrystallization behaviors of 58SiMn steel.
出处 《Chinese Journal of Mechanical Engineering》 SCIE EI CAS CSCD 2011年第3期446-451,共6页 中国机械工程学报(英文版)
关键词 static recrystallization mathematical model SIMULATION grain size 58SiMn steel static recrystallization mathematical model simulation grain size 58SiMn steel
  • 相关文献

参考文献9

二级参考文献35

  • 1[1]H.J.McQueen: J. Mater. Proc. Technol., 1993, 37(1-4), 3.
  • 2[2]T.Altan and V.Vazquez: Annuals of the CIRP, 1996, 2(45),599.
  • 3[3]J.J.Park and S.I.Oh: Journal of Engineering for Industry,Transactions of the ASME, 1990, 112(1), 36.
  • 4[4]M.Glowacki, Z.Kedzierski, H.Kusiak, W.Madei and M.Pietrzyk: J. Mater. Proc. Technol., 1992, 34(1-4), 509.
  • 5[5]N.Kim, S.M.Lee, W.Shin and R.Shivpuri: Journal of Engineering for Industry, Transactions of the ASME, 1992, 114(1), 329.
  • 6[6]R.Shivpuri and W.Shin: Int. J. Mach. Tools Manufact., 1992,32(5), 671.
  • 7[7]Xiaofeng DOU: Ph.D. Thesis, Univ. of Sci. & Tech. Beijing,1998, 44.
  • 8[8]S.M.Lee, W.Shin and R.Shivpuri: Int. J. Mach. Tools Manufact., 1992, 32(3), 315.
  • 9[9]Y.S.Jang, D.C.Ko and B.M.Kim: J. Mater. Proc. Technol.,2000, 101(1-3), 85.
  • 10[10]Yanwen WANG, Yonglin KANG, Zhiyong YU, Dahuan YUAN,Yuenan CHEN, Guofu WANG: Iron & Steel. 2000, 35(2), 38.

共引文献35

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部