摘要
介绍了热压陶瓷高速喷砂咀的研制, 着重研究了在热压温度为1450 ~1550 ℃, 热压压力为10 ~40 MPa情况下材料的致密比, 以及密度由4 .30 g/cm 3 增加到4 .60g/cm3 时材料的硬度和强度的变化情况。结果发现,随着温度的升高和压力的增大, 材料的密度有规律地增加; 随着密度的增加, 材料的硬度和强度增加。研制的陶瓷喷砂咀产品的性能如下: 密度4 .50 ~4 .60g/cm 3 , 硬度HRA92 ~94 , 抗弯强度700 ~900 MPa , 使用寿命1000 h
To deal with the high speed ceramic spray nozzle made by thermo pressing process, the densification of the nozzle material under the condition of 1 450~1 550 ℃ and 10~40 MPa pressure, and the hardness and strength of the material with 4.30~4.60 g/cm 3 density were investigated. The results show that the density of the material increases with the increase in thermo pressing temperature and pressure, and the hardness and strength of the material increase with the increase in the density. The characteristics of the nozzle are as follows: density 4.50~4.60 g/m 3, hardness HRA92-94, bending strength 700~900 MPa, and lifetime ≥1 000 h.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
1999年第3期562-566,共5页
The Chinese Journal of Nonferrous Metals
关键词
陶瓷
热压
喷砂咀
研制
ceramics
thermo pressing
spraying
nozzles