为得到电磁性能优良的碳纳米管,采用化学镀的方法在碳纳米管表面镀镍-钴-磷三元合金。利用透射电镜(TEM)、能谱分析(EDS)、振动样品磁强计(VSM)对施镀后的碳纳米管进行表征,发现所得镀层完整、均匀,为软磁材料。碳纳米管化学镀Ni-Co-P三元合金的电磁参数研究表明,其吸波机理主要为磁损耗。
In order to obtain carbon nanotubes with excellent electromagnetic properties,Ni-Co-P ternary alloy were plated on the surface of carbon nanotubes.The carbon nanotubes were characterized with TEM,EDS and VSM after electroless plating,which show that the coating was complete,uniform and soft magnetic materials.The electromagnetic nanotubes plated with Ni-Co-P ternary alloy have show that the absorbing mechanism was magnetic loss.