摘要
γ-LiAlO2：Eu3＋（Eu3＋：LAO） phosphor was obtained by gel combustion method using LiNO3,Al（NO3）3·9H2O,Eu（NO3）3·6H2O and citric acid as raw materials.The structure,morphology and luminescence were characterized by means of X-ray diffraction （XRD）,scanning electron microscopy （SEM）,photoluminescence （PL）.The results demonstrated that the phosphor was pure-phase of flaky tetragonal crystal system with a mean size of around 1 μm.The strongest excitation peak was at 254 nm,belonging to the broadband excitation and the maximum emission peak was at 613 nm,corresponding to the 5D0→7F2 transition of Eu3＋.Luminous intensity is closely related to the calcination temperature and doping concentration of Eu3＋.
γ-LiAlO2：Eu3＋（Eu3＋：LAO） phosphor was obtained by gel combustion method using LiNO3,Al（NO3）3·9H2O,Eu（NO3）3·6H2O and citric acid as raw materials.The structure,morphology and luminescence were characterized by means of X-ray diffraction （XRD）,scanning electron microscopy （SEM）,photoluminescence （PL）.The results demonstrated that the phosphor was pure-phase of flaky tetragonal crystal system with a mean size of around 1 μm.The strongest excitation peak was at 254 nm,belonging to the broadband excitation and the maximum emission peak was at 613 nm,corresponding to the 5D0→7F2 transition of Eu3＋.Luminous intensity is closely related to the calcination temperature and doping concentration of Eu3＋.
基金
Funded by Southwest University of Technology (No.08zx0103)