摘要
A polyether diol poly[3-bromomethyl-3-tridecafluorooctyloxymethyloxetane]glycol(PFBOX 3) was prepared in 91% yield from ring opening polymerization of 3-bromomethyl-3-tridecafluorooctyloxymethyloxetane 2 which was derived from 3,3-dibromomethyloxetane 1 and 1H,1H,2H,2H-perfluorooctanol.The waterborne fluorinated polyurethane FPU was thus obtained by condensed polymerization of PFBOX 3 with isophoronediisocyanate(IPDI).The structure of FPU was characterized by Fourier transform infrared spectrometer(FTIR).FPU showed good thermal stability under 300℃.The surface properties of FPU were studied by applied on cotton fabric.The treated fabric surface showed excellent water repellent property as the contact angle reached 147°.On the other hand,the surface showed slightly oil repellent property as the contact angle for nujol droplet was 126°.
A polyether diol poly[3-bromomethyl-3-tridecafluorooctyloxymethyloxetane]glycol（PFBOX 3） was prepared in 91% yield from ring opening polymerization of 3-bromomethyl-3-tridecafluorooctyloxymethyloxetane 2 which was derived from 3,3-dibromomethyloxetane 1 and 1H,1H,2H,2H-perfluorooctanol.The waterborne fluorinated polyurethane FPU was thus obtained by condensed polymerization of PFBOX 3 with isophoronediisocyanate（IPDI）.The structure of FPU was characterized by Fourier transform infrared spectrometer（FTIR）.FPU showed good thermal stability under 300℃.The surface properties of FPU were studied by applied on cotton fabric.The treated fabric surface showed excellent water repellent property as the contact angle reached 147°.On the other hand,the surface showed slightly oil repellent property as the contact angle for nujol droplet was 126°.
基金
Shanghai Municipal Scientific Committee,China (No. 08JC1400400)