摘要
通过对乙醛００Ｃｒ１７Ｎｉ１２Ｍｏ２废水线投用６个月后即发生腐蚀开裂原因的分析，认为在该种工况下，是工艺废水中氯离子浓度超标和施工质量等因素造成氯离子的应力腐蚀。
Acetaldehyde plant 00Crl7Ni12Mn2 waste line cracking occurred only after six months run length, the results of studyshowed, that the concentration of chlorion in process waste water is out of standard at the operating environment, and some factors in constructions cause the chlorion stress corrosion.
出处
《黑龙江石油化工》
1999年第4期35-36,42,共3页
Heilongjiang Petrochemical Technology