Polycrystalline La0.67Ba0.33MnO3 bulk samples were annealed in flowing 95%Ar：5%H2 （AH） mixed gas at 973 K for different time respectively. The influence of the annealing time on the current-voltage properties was systematically investigated. Linear current-voltage characteristics were observed in the as-prepared and the 10 h annealed samples, and nonlinear current-voltage characteristics was found in the 100 h annealed sample. At the same time, segregation of impurity phase and micro-cracks were found on the surfaces of the 100 h annealed samples, which was testified to be Ba ion impurity. Analysis showed that the changes of electronic properties were caused by barium ion im-purities and micro-cracks in the 100 h annealed sample.
Polycrystalline La0.67Ba0.33MnO3 bulk samples were annealed in flowing 95%Ar：5%H2 （AH） mixed gas at 973 K for different time respectively. The influence of the annealing time on the current-voltage properties was systematically investigated. Linear current-voltage characteristics were observed in the as-prepared and the 10 h annealed samples, and nonlinear current-voltage characteristics was found in the 100 h annealed sample. At the same time, segregation of impurity phase and micro-cracks were found on the surfaces of the 100 h annealed samples, which was testified to be Ba ion impurity. Analysis showed that the changes of electronic properties were caused by barium ion im-purities and micro-cracks in the 100 h annealed sample.
基金
supported by the National Natural Science Foundation of China (10975103)