摘要
A novel zinc coordination polymer, [Zn2(bptc)(bpe)(H2O)]n (1, Habptc = 3,3",4,4"- benzophenonetetracarboxylate, bpe = 1,2-bis(4-pyridyl) ethane), has been prepared under hydrothermal conditions. The crystal structure is of monoclinic, space group C/2c with a = 27.50(2), b = 6.207(4), c = 16.233(11) A, β = 107.522(14)°, V= 2642 (3) As, C29H22N2O11Zn2, Mr = 705.27, Z = 4, Dc = 1.773 g/cm3, F(000) = 1432, p = 1.887 mm-1, R = 0.0421 and wR = 0.1049 for 2594 observed reflections (I 〉 20(/)). X-ray single-crystal diffraction analysis shows that 1 features two-dimensional [Zn2(bptc)(H2O)] layers, which are further linked by the bpe ligands to give rise to a three-dimensional pillar-layered structure. According to the topology analysis, this framework can be simplified into a (4,6)-connected (4^4.6&2)(4^4.6^10.8) network.
A novel zinc coordination polymer, [Zn2(bptc)(bpe)(H2O)]n (1, Habptc = 3,3",4,4"- benzophenonetetracarboxylate, bpe = 1,2-bis(4-pyridyl) ethane), has been prepared under hydrothermal conditions. The crystal structure is of monoclinic, space group C/2c with a = 27.50(2), b = 6.207(4), c = 16.233(11) A, β = 107.522(14)°, V= 2642 (3) As, C29H22N2O11Zn2, Mr = 705.27, Z = 4, Dc = 1.773 g/cm3, F(000) = 1432, p = 1.887 mm-1, R = 0.0421 and wR = 0.1049 for 2594 observed reflections (I 〉 20(/)). X-ray single-crystal diffraction analysis shows that 1 features two-dimensional [Zn2(bptc)(H2O)] layers, which are further linked by the bpe ligands to give rise to a three-dimensional pillar-layered structure. According to the topology analysis, this framework can be simplified into a (4,6)-connected (4^4.6&2)(4^4.6^10.8) network.
基金
Supported by the 973 program (No.2007CB815302,2009CB939803)
the Chinese Academy of Sciences (No.KJCX2.YW.319 and KJCX2.YW.M10)
the Knowledge Innovation Program of the Chinese Academy of Sciences
the Fund of Fujian Key Laboratory of Nanomaterials (2006L2005)