TiCl4/MgCl2/clay compound catalyst was prepared by chemical reaction. Exfoliated polypropylene （PP）/clay nanocomposites were synthesized by in situ polymerization with this compound catalyst. Effects of polymerization temperature, polymerization time, propylene pressure, solvent consumption and pre-treat time of catalyst on catalyst activity and catalytic stereospecificity were studied. Under optimal conditions, activity of the nano-compound catalyst is about 88.3 kg/（mol Ti-h）. Isotacticity of PP obtained in the nanocomposites is in the range of 89%-99%, and its melting temperature is about 159℃. The weight-average molecular weight of PP can reach 6.7 × 10^5 - 7.8 × 10^5, and the molecular weight distribution is between 7.7 and 7.9.
TiCl4/MgCl2/clay compound catalyst was prepared by chemical reaction. Exfoliated polypropylene （PP）/clay nanocomposites were synthesized by in situ polymerization with this compound catalyst. Effects of polymerization temperature, polymerization time, propylene pressure, solvent consumption and pre-treat time of catalyst on catalyst activity and catalytic stereospecificity were studied. Under optimal conditions, activity of the nano-compound catalyst is about 88.3 kg/（mol Ti-h）. Isotacticity of PP obtained in the nanocomposites is in the range of 89%-99%, and its melting temperature is about 159℃. The weight-average molecular weight of PP can reach 6.7 × 10^5 - 7.8 × 10^5, and the molecular weight distribution is between 7.7 and 7.9.
基金
financially supported by the National Natural Science Foundation of China(Nos.20774098,50973123, 50503023)
the Scientific Research Startup Foundation of Qingdao University of Science and Technology