摘要
对ＡＩ－０．３５Ｓｃ合金中加入同含量的微量过渡族元素Ｚｒ、Ｔｉ，采用正交实验测定了这些含Ｚｒ、Ｔｉ元素的ＡＩ－Ｓｃ合金的高温（２７０℃）持久寿命，并应用扫描电镜，观察了断口形貌，分析断裂机理。
Adding different amount transition elements Zr. Ti to the Al-0.35Sc alloy, orthogonal design isused to measure high-temperature dulation life of the alloys containing Zr.Ti elements at 270℃ 60 MPa.Fracture morphology is observed by means of SEM, fracture mechanism is analysed.