Nanosized La2-xKxNiMnO6 catalysts with ABO3 type perovskite-like structure were prepared by auto-combustion method using citric acid as a ligand to control particle size and morphology.The structures and properties of these perovskite-like oxides were investigated by X-ray powder diffraction（XRD）and temperature-programmed reduction（TPR）.The catalytic activities for soot combustion were evaluated by temperature- programmed oxidation（TPO）with pure O2 and O2/NOx as oxidant,respectively.In the La2-xKxNiMnO6 catalysts,the partial substitution of K at A-site leads to an increase of the concentrations of high valence cation and oxygen vacancy,which enhance the catalytic activity for soot combustion.The optimal substitution amount of K was equal to x=0.4 among these samples.Tp（peak temperature）in O2-TPO profile was 420-C and Tp in O2/NOx-TPO profile was 370-C over La1.6K0.4NiMnO6 catalyst for soot particulates combustion under loose contact conditions between catalyst and soot.
Nanosized La2-xKxNiMnO6 catalysts with ABO3 type perovskite-like structure were prepared by auto-combustion method using citric acid as a ligand to control particle size and morphology.The structures and properties of these perovskite-like oxides were investigated by X-ray powder diffraction（XRD）and temperature-programmed reduction（TPR）.The catalytic activities for soot combustion were evaluated by temperature- programmed oxidation（TPO）with pure O2 and O2/NOx as oxidant,respectively.In the La2-xKxNiMnO6 catalysts,the partial substitution of K at A-site leads to an increase of the concentrations of high valence cation and oxygen vacancy,which enhance the catalytic activity for soot combustion.The optimal substitution amount of K was equal to x=0.4 among these samples.Tp（peak temperature）in O2-TPO profile was 420-C and Tp in O2/NOx-TPO profile was 370-C over La1.6K0.4NiMnO6 catalyst for soot particulates combustion under loose contact conditions between catalyst and soot.
基金
supported by the National Natural Science Foundation of China(No.20603016)
the Liaoning Provincial Science&Technology Project of China(No.20071074)