通过改变镀液还原剂的含量和加入定量的乙酸钠,研究对化学镀镍硼合金形貌和性能的变化。从晶体结构、镀层形貌、硬度和耐磨曲线等几方面来分析加入乙酸钠12g/L时,化学镀Ni-B合金镀层形貌和性能改善的原因。乙酸钠起到缓冲剂的作用,降低了化学镀Ni-B的镀速,提高了化学镀Ni-B的致密度,改善了镀层的质量从而提高镀层的各种性能。
In order to enhance the properties of electroless Ni-B, the changes in morphology and performance of electroless Ni-B alloy was studied by changing the contents of reducing agent and adding quantitative sodium acetate. The reasons of the morphology and performance of the electroless Ni-B were improved while adding sodium acetate 12 g/L are analyzed based on crystal structure, coating morphology, hardness, wear curves. It was found that sodium acetate as a buffer can reduce the deposition rate of the chemical plating Ni-B, increase the density of the chemical plating Ni-B, and improve the quality of coating in the process.
出处
《中国腐蚀与防护学报》
CAS
CSCD
北大核心
2011年第4期315-318,共4页
Journal of Chinese Society For Corrosion and Protection
基金
西南交通大学科技发展基金项目(2007B08)
吉林油田公司科技项目资助
关键词
化学镀Ni—B
晶体结构
表面形貌
磨损
electroless Ni-B, crystal structure, coating morphology, wear