水热-微乳液法制备钴、镍混合氧化物及其电化学电容性能研究
摘要
采用水热-微乳液法合成钴、镍混合氧化物,采用X-射线衍射(XRD)、扫描电静(SEM)、循环伏安、恒电流放电测试对样品形貌及电化学性能进行了表征和测试。研究结果表明,通过改变Co的掺杂量可以控制CoNi混合氧化物电化学性能。
参考文献4
-
1Gupta V., Gupta S., Miura N. Potentiostatically deposited nanostructured CoxNil-x layered double hydroxidesas electrode materials for redox-supercapacitors [J]. J. Power Sources, 2008, 175(1): 680-685.
-
2Fan Z., Chen J.H., Cui K.Z., Sun F., Xu Y., Kuang Y. F. Preparation and capacitive propertiesof cobalt-nickel oxides/carbon nanotube composites [J]. Electrochim. Acta, 2007, 52(9): 2959-2965.
-
3Bouessay I., Rougier A., Tarascon M.J. Electrochemically inactive nickel oxide as electrochromic material [J]. J. Electrochem. Soc., 2004, 151(6): H145-H152.
-
4Nam K.W., Lee E.S., Kim J.H., Lee Y.H., Kim K.B. Synthesis and electrochemical investigations of Ni1-xO thin films and Nil-xO on three-dimensional carbon substrates for electrochemical capacitors [J]. J. Electrochem. Soc., 2005,152(11): A2123-A2129.
-
1冯晓娟,石彦龙,邵前飞,金小青,李永燕.交联多孔结构Mn^(2+)掺杂聚苯胺/石墨烯复合材料的制备及超级电容特性[J].化学通报,2016,79(9):828-833. 被引量：2
-
2严鹏丽,李爱龙,张丙青,施晶莹,甘阳,李灿.电化学还原处理对碳纸形貌和电化学电容的影响（英文）[J].高等学校化学学报,2015,36(11):2304-2310. 被引量：2
-
3阙庭丽,李娟.MoO_3基纳米复合材料的制备及其电化学性能研究[J].化学研究与应用,2012,24(7):1069-1074. 被引量：4
-
4徐暘,包彦彦,杜龙飞,曹殿学,王贵领.钙钛矿La1-xSrxCoO3的电化学电容性能[J].电化学,2013,19(2):174-177. 被引量：1
-
5张子瑜,胡中爱,杨玉英,王欢文,常艳琴,陈艳丽,雷自强.Ce掺杂Mn3O4及其电化学电容行为[J].物理化学学报,2011,27(7):1673-1678. 被引量：6
-
6米红宇,张校刚,吴全富.聚合温度对乙酸掺杂聚苯胺电化学电容行为的影响[J].高分子材料科学与工程,2007,23(4):128-131. 被引量：1
-
7陈玉华,戴亚堂,王伟,张欢,申振,马丽.氧化石墨烯/聚苯胺纳米线复合材料的制备及电化学电容性能研究[J].武汉理工大学学报,2013,35(9):25-29. 被引量：2
-
8马池,孔令斌,罗永春,康龙.Co(OH)_2/NaY复合材料的制备及其超级电容性能[J].电化学,2008,14(3):335-339.
-
9魏炳瑞.聚吡咯/二氧化锰复合材料的合成及电化学性能研究[J].化工管理,2015(34):175-175.
-
10杜然,张学同.烷氧磺酸盐功能化的聚乙撑二氧噻吩水凝胶(英文)[J].物理化学学报,2012,28(10):2305-2314.