摘要
分析T10钢冲模裂纹形态、化学成分、低倍和高倍金相组织,找出开裂原因,提出改进措施。
Analyzing the cracking form of T10 steel dies, chemical composition, low and high magnification microstrueture, the cracking reasons are found and the improvement measures are put forward.
出处
《热处理技术与装备》
2011年第4期50-51,共2页
Heat Treatment Technology and Equipment
关键词
冲模裂纹
原因分析
改进措施
die crack
Cause analysis
improvement measures