有机硅氧烷双重改性水性环氧乳液的研究 被引量:5

Research of Waterborne Epoxy Resin Emulsion with KH570 and KH550 Hybrid Modifier
下载PDF
导出
摘要 采用有机硅烷单体KH570和KH550双重改性水性环氧乳液,通过FT-IR、TGA、接触角测量仪对KH550、KH570改性所得产物及其涂膜进行表征,对改性后水性环氧乳液固化涂膜的微观结构及宏观性能进行了研究。结果表明:当KH570与KH550含量占环氧树脂的质量分数比为5∶1时,双重改性环氧乳液具有良好的贮存稳定性,其固化涂膜的耐水性、柔韧性和耐热性能得到很大改善。 A stable waterborne epoxy resin emulsion was modified by γ -methacryloxypropyl trimethoxy silane (KH570) and aminopropyltriethoxy silane (KH550). The modification effects in term of its microstructure and macro performance was investigated by FT -IR, TGA and contact angletest. The result showed that when the weight fraction of KH570 was 5% while KH550 was 1% (based on epoxy resin weight), the films obtained from the dispersion showed good storage stability and improved water resistance, flexility and thermal stability.
出处 《涂料工业》 CAS CSCD 北大核心 2011年第9期41-44,共4页 Paint & Coatings Industry
关键词 有机硅氧烷 环氧树脂 接枝 改性 接触角 siloxane epoxy resin graft modify contact angle
  • 相关文献

参考文献6

二级参考文献38

共引文献43

同被引文献628

引证文献5

二级引证文献27

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部