摘要
A new 3D metal-organic framework of {[Co3（IDC）2（bipy）2（py）2]·7H2O}n （1） was obtained by the hydrothermal reaction of Co（NO3）2·6H2O, imidazole-4,5-dicarboxylic acid （H3IDC）, 4,4＇-bipyridine （bipy）, and pyridine （py）, and structurally characterized by elemental analysis, infrared spectroscopy, thermal gravimetric analysis, and single-crystal X-ray diffraction. X-ray diffraction crystal structural analysis reveals that it crystallizes in orthorhombic system, space group Pccn with a = 11.1040（3）, b = 19.8834（5）, c = 21.3025（5）, V = 4703.3（2）3, Mr = 1079.63, Z = 4, Dc = 1.525 Mg·m-3, F（000） = 2212, μ（CuKα） = 8.855 mm-1, the final R = 0.0331 and wR = 0.0713 for 2525 observed reflections with I ≥ 2σ（I）. In compound 1, each cobalt（II） ion is six-coordinated with a slightly distorted octahedral coordination geometry, and each μ3-IDC3- acts as a bridge to bond three neighboring Co（II） ions, leading to an infinite 2D network layer structure of [Co3（IDC）2]n with Kagomé lattice. The adjacent layers are further linked by μ2-bipy to form an infinite 3D layered-pillared framework architecture of [Co3（IDC）2（bipy）2（py）2]n.
A new 3D metal-organic framework of {[Co3（IDC）2（bipy）2（py）2]·7H2O}n （1） was obtained by the hydrothermal reaction of Co（NO3）2·6H2O, imidazole-4,5-dicarboxylic acid （H3IDC）, 4,4＇-bipyridine （bipy）, and pyridine （py）, and structurally characterized by elemental analysis, infrared spectroscopy, thermal gravimetric analysis, and single-crystal X-ray diffraction. X-ray diffraction crystal structural analysis reveals that it crystallizes in orthorhombic system, space group Pccn with a = 11.1040（3）, b = 19.8834（5）, c = 21.3025（5）, V = 4703.3（2）3, Mr = 1079.63, Z = 4, Dc = 1.525 Mg·m-3, F（000） = 2212, μ（CuKα） = 8.855 mm-1, the final R = 0.0331 and wR = 0.0713 for 2525 observed reflections with I ≥ 2σ（I）. In compound 1, each cobalt（II） ion is six-coordinated with a slightly distorted octahedral coordination geometry, and each μ3-IDC3- acts as a bridge to bond three neighboring Co（II） ions, leading to an infinite 2D network layer structure of [Co3（IDC）2]n with Kagomé lattice. The adjacent layers are further linked by μ2-bipy to form an infinite 3D layered-pillared framework architecture of [Co3（IDC）2（bipy）2（py）2]n.
基金
supported by the National Natural Science Foundation of China (No. 21071099)