摘要
采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。
The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are changed from {110} 001 texture in subsurface to α fiber in 1/2 layer,and the intensity of {110} 001 texture is maximum in 1/4 layer of hot rolling strip.
出处
《金属功能材料》
CAS
2011年第4期1-5,共5页
Metallic Functional Materials
关键词
取向硅钢
热轧
析出物
织构
grain-oriented silicon steel
hot rolling
precipitates
texture