摘要
In general, during the production of compacted graphite iron (CGI), the active residual magnesium reduces and the effect of inoculation fades after magnesium treatment. In this paper, characteristics of the thermal analysis curve of CGI are compared with those of ductile iron and grey cast iron. The fading effect on the compacted graphite percentage and thermal analysis curve were also studied. Results indicate that the undercooling of CGI is as low as that of ductile iron, but CGI shows evident recalescence. In fading process, the magnesium element acts with oxygen. For a decrease in magnesium content, both the compacted graphite percentage and the austenitic liquidus temperature increase. The temperature of eutectic undercooling (TEU) decreases before the flake graphite appears. After that, TEU increases quickly, up to as high as 20℃, and then gradually decreases. The evolution of recalescence degree is opposite to that of TEU.
In general, during the production of compacted graphite iron （CGI）, the active residual magnesium reduces and the effect of inoculation fades after magnesium treatment. In this paper, characteristics of the thermal analysis curve of CGI are compared with those of ductile iron and grey cast iron. The fading effect on the compacted graphite percentage and thermal analysis curve were also studied. Results indicate that the undercooling of CGI is as low as that of ductile iron, but CGI shows evident recalescence. In fading process, the magnesium element acts with oxygen. For a decrease in magnesium content, both the compacted graphite percentage and the austenitic liquidus temperature increase. The temperature of eutectic undercooling （TEu） decreases before the flake graphite appears. After that, TEU increases quickly, up to as high as 20℃, and then gradually decreases. The evolution of recalescence degree is opposite to that of TEu.
关键词
压缩石墨铁
热分析
褪色
压缩石墨百分比
典型价值
compacted graphite iron
thermal analysis
fading
compacted graphite percentage
characteristicvalue