用磁控溅射镀膜方法,制备掺杂WO3的ITO(xWO3-ITO)薄膜,经过热处理后对掺杂薄膜的表面形貌、吸收和透射光谱、面电阻等性能进行了测试。结果表明:适当的热处理能够提高xWO3-ITO薄膜在可见光范围内的透过率和在波长为228nm处的吸光度。同时,该薄膜热处理后的方块电阻明显降低,导电性能得到明显提高。
The preparation of WO3-doped ITO （xWO3-ITO） thin film was made by magnetron sputte- ring. After annealing, the properties of the doped thin films were tested such as surface morphology, absorption and transmittance spectrum and conductivity. The results show that the proper annealing can improve the transmittance of the xWO3-ITO thin films in the visible range and the absorption of the films in the wavelength of 228 nm and that through annealing, the sheet resistance of the films de- creases obviously while the electrical performance is improved remarkably.