根据国标GB/T 8650-2006《管线钢和压力容器钢抗氢致开裂评定方法》,对管线钢抗氢致开裂(H IC)性能试验方法进行了研究,试验中通过采用一系列措施,保证了试验人员安全的同时顺利完成试验,取得了满意效果。
According to the national standard GB/T 8650 -2006《Evaluation of pipeline and pressure vessel steels for resistance to hydrogen cracking》, hydrogen - induced cracking of pipeline steel was researched, during which a series of measures were taken to guarantee personnel safety and test succession and at the same time satisfactory effect achieved.