Nano-silver loaded montmorillonite （Ag-MMT） was prepared by ion-exchange and then a UV-photoreduction two-step approach was applied. The silver content in Ag-MMT determined by Volhard method was about 6.4 wt%. The morphology and structure of as-synthesized Ag-MMT were characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The results showed that the Ag nanoparticles were spherical and their diameters were about 15-20 nm. Moreover, the structure of MMT did not change. The minimum inhibition concentration （MIC） of Ag-MMT was 100×10-6 and the sterilizing efficiency （SE） of Ag-MMT was approximately 100% against Escherichia coli ATCC 11229 （E. coli. In addition, the slow release property of silver in Ag-MMT was also demonstrated.
Nano-silver loaded montmorillonite （Ag-MMT） was prepared by ion-exchange and then a UV-photoreduction two-step approach was applied. The silver content in Ag-MMT determined by Volhard method was about 6.4 wt%. The morphology and structure of as-synthesized Ag-MMT were characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The results showed that the Ag nanoparticles were spherical and their diameters were about 15-20 nm. Moreover, the structure of MMT did not change. The minimum inhibition concentration （MIC） of Ag-MMT was 100×10-6 and the sterilizing efficiency （SE） of Ag-MMT was approximately 100% against Escherichia coli ATCC 11229 （E. coli. In addition, the slow release property of silver in Ag-MMT was also demonstrated.
基金
Huazhong University of Science and Technology,China, for the analytical support