固溶温度对690合金在NaOH溶液中的电化学性能影响 被引量:2

Effect of heat treatment on electrochemical behavior of alloy 690 in NaOH solution
下载PDF
导出
摘要 采用SEM方法研究不同温度固溶处理的690合金组织结构,利用动电位极化、电化学阻抗和局部电化学交流阻抗(LEIS)等方法研究了其在NaOH溶液中的电化学行为。SEM结果表明,固溶处理温度1095℃的690合金的晶粒较大,晶界上分布着连续的碳化物。极化曲线结果表明,固溶处理温度1090℃的690合金在氢氧化钠溶液中的电流密度最大;电化学阻抗表明,固溶处理温度1100℃的690合金在氢氧化钠溶液中的阻抗模值较大。局部电化学交流阻抗谱表明,不同温度固溶处理的690合金在氢氧化钠溶液中的电化学阻抗具有明显不同的分布特征。 Microstructure of alloy 690 solid-solutioned at different temperatures was investigated by SEM.Electrochemical behavior of alloy 690 in NaOH solution was examined by means of potentiodynamic polarization,electrochemical impedance spectroscopy(EIS) and localized electrochemical impedance spectroscopy(LEIS).SEM result shows that grain size of alloy 690 solution-treated at 1095 ℃ is larger than that of the alloy treated at 1090 ℃ and 1100 ℃.Carbides at grain boundaries are observed in the alloy solution-treated at different temperatures.It is shown that the alloy 690 solutioned at 1090 ℃ exhibits the largest corrosion current density in NaOH solution.EIS result indicates that the impedance value of alloy 690 solutioned at 1100 ℃ in NaOH solution is higher than other specimens.LEIS results demonstrate that the surface localized electrochemical impedance spectroscopy of alloy 690 heat treated at different temperatures presents different distribution feature.
出处 《材料热处理学报》 EI CAS CSCD 北大核心 2011年第9期48-52,共5页 Transactions of Materials and Heat Treatment
基金 国家高技术研究发展("863")计划(2008AA031703) 国家科技基础条件平台建设项目(2005DKA10400)
关键词 690合金 固溶处理 SEM 电化学阻抗 局部电化学交流阻抗 690 alloy solid solution freatment SEM electrochemical impedance spectroscopy(EIS) localized electrochemical impedance spectroscopy(LEIS)
  • 相关文献

参考文献17

  • 1Copson H R, Dean S W. Effect of contaminants on resistance to stress corrosion cracking of Ni-Cr alloy 600 in pressurized water[ J]. Corrosion, 1965, 21(1): 1-8.
  • 2Dutta R S, Tewari R, De P K. Effects of heat-treatment on the extent of chromium depletion and caustic corrosion resistance of alloy 690 original research[J]. Corrosion Science, 2007, 49(2) : 303 -318.
  • 3Casales M, Salinas-Bravo V M, Martinea-Villafane A, et al. Effect of heat treatment on the stress corrosion cracking of alloy 690 [ J]. Materials Science and Engineering A, 9002, 332 ( 1 - 2) :223 - 230.
  • 4Ahn M K, Kwon H S, Lee J H. Predicting IGSCC Susceptibility of Alloy 600 by Modified EPR Test [J]. Corrosion, 1995, 51(6) :441.
  • 5Was G S,Rajan V B. Mechanism of intergranular cracking of Ni-Cr-Fe alloys in sodium tetrathionate [ J]. Metallurgical Transactions A, 1987,18: 1313.
  • 6Crum J R. Stress corrosion cracking testing of INCONEL alloys 600 and 690 under high-temperature caustic conditions[ J]. Corrosion, 1986,42:368.
  • 7Staehle R W, Gorman J A. Quantitative assessment of submodes of stress corrosion cracking on the secondary side of steam generator tubing in pressurized water reactors: part 1 [ J]. Corrosion, 2003, 59 ( 11 ) : 931 - 940.
  • 8Staehle R W, Gorman J A. Quantitative assessment of submodes of stress corrosion eraeking on the secondary side of steam generator tubing in pressurized water reactors: part 2 [ J ]. Corrosion, 2004, 60 ( 1 ) : 5 - 63.
  • 9Staehle R W, Gorman J A. Quantitative assessment of submodes of stress corrosion cracking on the secondary side of steam generator tubing in pressurized water reactors: Part 3 [ J ]. Corrosion, 2004, 60 (2) : 115 - 180.
  • 10Ahn Se Jin, Shankar Rao V, Kwon Hyuk Sang, et al. Effects of PbO on the repassivation kinetics of alloy 690[ J ]. Corrosion Science, 2006,48 (5) : 1137 - 1153.

二级参考文献11

  • 1Parvathavarthini N,Dayal R K.Influence of chemical composition,prior deformation and prolonged thermal aging on the sensitization characteristics of austenitic stainless steels[J].Nuclear Materials,2002,305:209-219.
  • 2Murr L E,Advani A,Shankar S,et al.Effects of deformation (strain) and heat treatment on grain boundary sensitization and precipitation in austenitics stainless steels[J].Materials Characterization,1990,24:135-158.
  • 3Almanza E,Murr L E.A comparison of sensitization kinetics in 304 and 316 stainless steels[J].Materials Science,2002,35(13):3181-3188.
  • 4Li D,Mao X.Stress corrosion cracking of long term ageing-treated 316 stainless steel in boiling 42% MgCl2 solution[J].Materials Science Letters,1997,16 (3):244-247.
  • 5季祥民,高宝东,陈斌.碳和磷及其固溶处理制度对316L不锈钢耐蚀性的影响[C].第九届全国不锈钢年会论文集,1992,152-160.
  • 6王振樵,吴幼林.不锈钢[M].北京:化学工业出版社,1991,5.
  • 7Hong H U,Nam S W.The occurrence of grain boundary serration and its effect on the M23 C6 carbide characteristics in an AISI 316 stainless steel[J].Materials Science and Engineering,2002,A332:255-261.
  • 8Kima K J,Ginsztlerb J,Nam S W.The role of carbon on the occurrences of grain boundary serration in an AISI 316 stainless steel during aging heat treatment[J].Materials Science Letters,2005,59:1439-1443.
  • 9肖继美.合金相与相变[M].北京:冶金工业出版社,1987:239.
  • 10王荣光,魏云,张清廉,郑文龙.奥氏体不锈钢SUS316及SUS316L在含Cl^-的饱和H_2S水溶液中的应力腐蚀行为研究[J].中国腐蚀与防护学报,2000,20(1):47-53. 被引量:35

共引文献14

同被引文献29

  • 1Copson H R, Dean S W. Effect of contaminants on resistance to stress corrosion cracking of Ni-Cr alloy 600 in pressurized water[ J]. Corrosion, 1965, 21(1): 1-8.
  • 2Durra R S,Tewari R, De P K. Effects of heat-treatment on the extent of chromium depletion and caustic corrosion resistance of alloy 690 original research [ J ]. Corrosion Science,2007,49 ( 2 ) : 303 - 318.
  • 3Casales M, Salinas-Bravo V M, Martinea-Villafane A, et al. Effect of heat treatment on the stress corrosion cracking of alloy 690 [ J]. Materials Science and Engineering A,2002,332 ( 1 - 2 ) : 223 - 230.
  • 4Dutta R S, Tewafi R, De P K. Effects of heat-treatment on the extent of chromium depletion and caustic corrosion resistance of alloy 690 [ J]. Corrosion Science,2007,49 (2) :303 - 318.
  • 5Was G S, Rajan V B. Mechanism of intergranular cracking of Ni-Cr-Fe alloys in sodium tetrathionate [ J ]. M etall Trans A, 1987,18 (7) :1313 -1323.
  • 6Was G S. Grain boundary chemistry and intergranular fracture in austenitic nickel-base alloys[ J]. Materials Science Forum, 1989,46:335 -358.
  • 7Kim U C,Kim K M, Lee E H. Effects of chemical compounds on the stress corrosion cracking of steam generator tubing materials in a caustic solution [ J ]. Journal of Nuclear Materials ,2005,341 ( 2 ) : 169 - 174.
  • 8Peng B,Lu B T,Luo J L,et al. Investigation of passive films on nickel Alloy 690 in lead-containing environments[ J ]. Journal of Nuclear Materials, 2008,378(3) :333 - 340.
  • 9Xia S,Zhou B X, Chert W J. Grain cluster microstructure and grain boundary character distribution in alloy 690 [ J]. Metallurgical and Materials Transactions A ,2009,40 ( 12 ) :3016 - 3030.
  • 10Li H, Xia S ,Zhou B, et al. C-Cr segregation at grain boundary before the carbide nucleation in alloy 690 [ J]. Materials Chatacte ,2012,27 (3) :68 -74 Shimada M, Kokawa H, Wang Z J, et al. Optimization of grain boundary character distribution for intergranular corrosion resistant of 304 stainless steel by twin-induced grain boundary engineering [ J ]. Acta Materialia,2002,50 ( 9 ) :2331 - 2341.

引证文献2

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部