天然红柱石莫来石化后热喷涂粉末的制备 被引量:2

Preparation of thermal spray powders using mullitized natural andalusite
下载PDF
导出
摘要 为获得莫来石热喷涂粉末,采用天然红柱石粉末作为原料,在1480℃保温4 h完成一次莫来石化后,加入适量Al2O3再次在1480℃保温4 h进行二次莫来石化反应,利用喷雾干燥工艺制备莫来石粉末,分析了红柱石粉末和莫来石化粉末的成分及相组成,测试了粉末粒度分布,表征了粉末的形貌.结果表明:天然矿物红柱石粉末一次莫来石化后,粉末主要由莫来石和质量分数约20%的SiO2组成;经过二次莫来石化反应后,粉末成分为莫来石和微量的Al2O3;二次莫来石化的粉末经喷雾干燥、热处理后,粉末的流动性和松装密度得以改善;热处理后粉末粒度呈典型的正态分布,且粒径尺寸适合大气等离子喷涂. To obtain mullite thermal spray powders,natural andalusite powders were annealed at 1480℃in air for 4 h to promote their mullitization,then,after adding an appropriate amount Al 2 O3 powders,the secondary mullitization was carried out.The mullitized powders were prepared by spray-dried process.The component and phase structure of the powders before and after mullitzation were analyzed,the size distribution of the powders was tested,and the morphology of spray-dried powders was investigated.The results showed that the primary mullitized andalusite powders contained mullite and about 20wt%SiO2.After the secondary mullitization,the powders were constituted of mullite and a limited amount of Al 2 O3.The fluidity and apparent density of spray-dried powders were improved by heat-treatment,and its typical size distribution was suitable for air plasma spray.
出处 《材料科学与工艺》 EI CAS CSCD 北大核心 2011年第4期107-111,共5页 Materials Science and Technology
基金 国家自然科学基金委创新研究群体科学基金资助项目(50421502) 国家重点基础研究发展计划资助项目(2007CB607601)
关键词 红柱石 莫来石化 莫来石 喷雾干燥 andalusite mullitzation mullite spray-dried
  • 引文网络
  • 相关文献

参考文献10

  • 1CIPRI F, BARTULI C, VALENTE T, et al, Electromagnetic and mechanical properities of silica-aluminosilicates plasma sprayed composite coatings [ J ]. Journal of Thermal Spray Technology, 2007, 16(5/6) :831 -838.
  • 2SCHNEIDER H, SCHREUER J,HULDMANN B. Structure and properties of mullite - A review [ J ]. Journal of the European Society, 2008, 28:329 - 344.
  • 3侯平均,黄国鹏,王汉功,汪刘应.微弧等离子喷涂制备莫来石/金属复合热障涂层[J].焊接学报,2009,30(5):85-88. 被引量:4
  • 4SCHNEIDER H, OKADA K, PASK J A. Mullite and Mullite Ceramics [ M ]. New York : Wiley, 1994.
  • 5曹雪强.热障涂层材料[M].北京:科学出版社,2007:161.
  • 6WIGREN J, GREVING D, DEVRIES F. J. Effects of powder morphology, microstructure and residual stresses on the thermal barrier coating thermal shock performance [ C ]//9th NTSC, Cincinnati : ASM International, 1996 : 855 - 861.
  • 7BOUCHETOU M L, ILDEFONSE J P, POIRIER J, et al. Mullite grown from fired andalusite grains: the role of impurities and of the high temperature liquid phase on the kinetics of mullitization and consequences on thermal shocks resistance [ J ]. Ceramics International, 2005, 31,999 - 1005.
  • 8SCHNEIDER H, KOMARNENI S. Mullite [ M ]. Wiley VCH : Weinheim, 2005.
  • 9ANGELINK H, MARTIN S, WERNER M, et al. The transformation of andalusite to mullite and silica: Part I. Transformation mechanism in [ 001 ] A direction [ J ]. American Mineralogist,2000,85:980 - 986.
  • 10李柳生,平增福.红柱石的莫来石化[J].硅酸盐通报,2006,25(1):34-36. 被引量:13

二级参考文献12

共引文献15

同被引文献8

引证文献2

二级引证文献5

;
使用帮助 返回顶部