Natural rubber （NR）/multi-walled carbon nanotube （MWCNTs） composites were prepared by combining self-assembly and latex compounding techniques.The acid-treated MWCNTs （H2SO4：HNO3=3：1,volume ratio） were self-assembled with poly （diallyldimethylammonium chloride） （PDDA） through electrostatic adhesion.In the second assembling,NR/MWCNTs composites were developed by mixing MWCNTs/PDDA solution with NR latex.The results show that MWCNTs are homogenously distributed throughout the NR matrix as single tube and present a great interfacial adhesion with NR phase when MWCNTs contents are less than 3 wt%.Moreover,the addition of the MWCNTs brings about the remarkable enhancement in tensile strength and crosslink density compared with the NR host,and the data peak at 2 wt% MWCNTs loadings.When more MWCNTs are loaded,aggregations of MWCNTs are gradually generated,and the tensile strength and crosslink both decrease to a certain extent.
Natural rubber （NR）/multi-walled carbon nanotube （MWCNTs） composites were prepared by combining self-assembly and latex compounding techniques.The acid-treated MWCNTs （H2SO4：HNO3=3：1,volume ratio） were self-assembled with poly （diallyldimethylammonium chloride） （PDDA） through electrostatic adhesion.In the second assembling,NR/MWCNTs composites were developed by mixing MWCNTs/PDDA solution with NR latex.The results show that MWCNTs are homogenously distributed throughout the NR matrix as single tube and present a great interfacial adhesion with NR phase when MWCNTs contents are less than 3 wt%.Moreover,the addition of the MWCNTs brings about the remarkable enhancement in tensile strength and crosslink density compared with the NR host,and the data peak at 2 wt% MWCNTs loadings.When more MWCNTs are loaded,aggregations of MWCNTs are gradually generated,and the tensile strength and crosslink both decrease to a certain extent.
基金
Funded by the National Natural Science Foundation of China (No.50763006)
Ministry of Science and Technology R & D Research Institutes (No.2008EG134285)
973 Program Special Fund (No.2010CB635109)