The effect of austenite aging at 823 K on the microstructures and martensitic transformation behavior of Co 46 Ni 27 Ga 27 alloy has been investigated using optical microscopy （OM）, transmission electron microscopy （TEM）, X-ray diffraction analysis （XRD）, and differential scanning calorimeter （DSC）. The microstructure observation results show that the unaged Co 46 Ni 27 Ga 27 alloy is composed of the tetragonal nonmodulated martensite phase and face-centered cubic γ phase. It is found that a new nanosized fcc phase precipitates in the process of austenite aging, leading to the formation of metastable age-affected martensite around the precipitates with composition inhomogeneity. Two-stage reverse martensitic transformation occurs in the samples aged for 2 and 24 h due to the composition difference between the age-affected martensite and the original martensite. For the Co 46 Ni 27 Ga 27 alloy aged for 120 h, no reverse transformation can be detected due to the disappearance of the metastable age-affected martensite and the small latent heat of the original martensite. The martensitic transformation temperatures of the Co 46 Ni 27 Ga 27 alloy decrease with an increase in aging time.
The effect of austenite aging at 823 K on the microstructures and martensitic transformation behavior of Co 46 Ni 27 Ga 27 alloy has been investigated using optical microscopy （OM）, transmission electron microscopy （TEM）, X-ray diffraction analysis （XRD）, and differential scanning calorimeter （DSC）. The microstructure observation results show that the unaged Co 46 Ni 27 Ga 27 alloy is composed of the tetragonal nonmodulated martensite phase and face-centered cubic γ phase. It is found that a new nanosized fcc phase precipitates in the process of austenite aging, leading to the formation of metastable age-affected martensite around the precipitates with composition inhomogeneity. Two-stage reverse martensitic transformation occurs in the samples aged for 2 and 24 h due to the composition difference between the age-affected martensite and the original martensite. For the Co 46 Ni 27 Ga 27 alloy aged for 120 h, no reverse transformation can be detected due to the disappearance of the metastable age-affected martensite and the small latent heat of the original martensite. The martensitic transformation temperatures of the Co 46 Ni 27 Ga 27 alloy decrease with an increase in aging time.
基金
supported by the Science Fund for Creative Research Groups of the National Natural Science Foundation of China (No. 50921003)
the National Natural Science Foundation of China (No. 51101057)
the Fundamental Research Funds for the Central Universities (No. 09QG41)