使用2A02H112φ25mm影响,通过试验调整桨叶锻件热处理制度,使产品满足标准要求,应用于生产取得良好效果。:冷拉棒材做毛料的桨叶锻件的热处理工艺,首次提出了退火。
The heat treatment processes of 2A02H110 Φ25mm cold-drawn bars and blades forgings forged by the cold-drawn bars were studied.The effect of annealing and cold-drawing on the subsequent heat treatment was analyzed,and the heat treatment process for blades forgings was adjusted by the test.