摘要
Transparent conductive indium tin oxide （ITO） nanoparticles were synthesized by a novel sol-gel method. Granulated indium and tin were dissolved in HNO3 and partially complexed with citric acid. A sol-gel process was induced when tertiary butyl alcohol was added dropwise to the above solution. ITO nanopartides with an average crystallite size of 18.5 nm and surface area of 32.6 m^2 ]g were obtained after the gel was heat-treated at 700 ℃, The ITO nanoparticles showed good sinterability, the starting sintering temperature decreased sharply to 900 ℃, and the 1400 ℃ sintered pellet had a density of 98.1% of theoretical density （TD）.
Transparent conductive indium tin oxide （ITO） nanoparticles were synthesized by a novel sol-gel method. Granulated indium and tin were dissolved in HNO3 and partially complexed with citric acid. A sol-gel process was induced when tertiary butyl alcohol was added dropwise to the above solution. ITO nanopartides with an average crystallite size of 18.5 nm and surface area of 32.6 m^2 ]g were obtained after the gel was heat-treated at 700 ℃, The ITO nanoparticles showed good sinterability, the starting sintering temperature decreased sharply to 900 ℃, and the 1400 ℃ sintered pellet had a density of 98.1% of theoretical density （TD）.
基金
supported by grants from Ph.D. Programs Foundation of Ministry of Education of China (200802511022)
National Natural Science Foundation of China (50902049)