贝氏体车轮钢的氢脆敏感性 被引量:3

Hydrogen Embrittlement Sensitivity of a Bainite Railway Wheel Steel
下载PDF
导出
摘要 用电解充氢试验方法研究了可扩散氢浓度对贝氏体车轮钢慢拉伸性能及氢致滞后开裂性能的影响,并与普通珠光体-铁素体车轮钢进行了对比。结果表明,在相同慢拉伸条件下,贝氏体车轮钢材料的塑性损失高于珠光体-铁素体车轮钢;在相同的充氢条件下,贝氏体车轮钢氢致开裂门槛应力强度因子相对于断裂韧性值的降低程度明显高于珠光体-铁素体车轮钢,具有较高的氢致开裂敏感性。 The influence of diffusible hydrogen concentration (Co) on the plasticity and hydrogen induced delayed cracking of a bainite railway wheel steel was investigated by means of the slow strain rate test (SSRT) specimens and wedge open loading (WOL) specimens charged in a solution respectively. The results showed that the plasticity loss of the bainite wheel steel was larger than that of the pearlite-ferrite CL60 wheel steel. The threshold stress intensity factor of hydrogen induced delayed cracking K1, of the bainitie wheel steel decreased with the increase of diffusible hydrogen concentration. The Km of the bainite wheel steel was much lower than that of the CL60 wheel steel when C0≥1.6 × 10-6, though the fracture toughness KIC of the bainite wheel steel was much higher than that of the CL60 wheel steel.
出处 《腐蚀与防护》 CAS 北大核心 2011年第11期863-867,共5页 Corrosion & Protection
基金 国家自然科学基金资助项目(50901010) 高等学校博士学科点专项科研基金资助项目(200800081006)
关键词 贝氏体 车轮钢 氢脆 氢致滞后开裂 bainite wheel steel hydrogen embrittlement hydrogen induced delayed cracking
  • 引文网络
  • 相关文献

参考文献4

  • 1贺信莱,尚成嘉,杨善武等.高性能低碳贝氏体钢[M].北京:冶金工业出版社,2008.
  • 2Zhang M R,Gu H C. Microsturcture and properties of carbide free bainite railway wheels produced by pro- grammed quenching[J]. Materials Science an Technol- ogy, 2007,23 (8) : 970-974.
  • 3江波,陈刚,刘芬斌,任学冲,褚武扬.含硅低合金高强度贝氏体钢的环境断裂敏感性[J].腐蚀与防护,2010,31(9):665-669. 被引量:1
  • 4Ren X C,Chu W Y,Su Y J,et al Effects of atomic hy- drogen and flacking on mechanical properties of wheel steel[J]. Metallurgical and Materials Transactions, 2007,38(A) : 1004--1011.

二级参考文献2

共引文献32

同被引文献32

  • 1李国韬,刘飞,宋桂华,温庆和.大张坨地下储气库注采工艺管柱配套技术[J].天然气工业,2004,24(9):156-158. 被引量:13
  • 2崔教林,D.Hardie.三种钢的氢脆敏感性探讨[J].腐蚀与防护,1996,17(3):114-117. 被引量:3
  • 3谭文志 杜元龙 傅超 等.阴极保护导致ZC-120钢在海水中环境氢脆.材料保护,1988,21(3):10-13.
  • 4褚武杨 乔利杰 陈奇志.断裂与环境断裂[M].北京:科学出版社,2000..
  • 5TSAY L W, YANG T Y, YOUNG M C. Embrittle ment of laser surfaceannealed 17-4PH stainless steel [J]. Materials Science and Engineering A, 2001, 311 (1/2): 64 -73.
  • 6CHIANG W C, PU C C, YU B L, et al. Hydrogen susceptibility of 17 4PH stainless steel[J]. Materials Letters, 2003, 57(16/17): 2485-2488.
  • 7ADAMS T M, MICKALONIS J. Hydrogen permea- bility of multiphase V-Ti-Ni metallic membranes [J]. Materials Letters, 2007, 61(3).. 817-820.
  • 8TAKANO T, OSHIKAWA K, MATSUDA T, et al. Hydrogen permeation of eutectic Nb-Zr-Ni alloys membranes containing primary phasesFJ]. Journal of Alloys and Compound, 2004, 45(12) : 458-461.
  • 9HIROKI I. Hydrogen embrittlement of high strength martensitic stainless steels [J]. Sanyo Technical Re port, 2002, 9(1): 50 -58.
  • 10CAPELLE J, GILGERT J, DMYTRAKH I, et al. Sensitivity of pipelines with steel API X52 to hydrogen embrittlement[J]. International Journal of Hydrogen Energy, 2008, 33(24).. 7630-7641.

引证文献3

二级引证文献18

;
使用帮助 返回顶部