The electro-deposition method was used for preparation of nanocrystalline Ni-W alloys coating. The formation, microstructure and performance of the nanocrystalline were investigated. X-ray diffraction results show that Ni-W alloys are crystallized in scale of 1730nm. Changing with the depositional time, the coating varies with different surface morphology. The observation on the formation of the coating implies that, the alloys preferentially deposit and grow on the scratch and corrosion pit edges. The hardness of the alloy coatings is related to the solution composition, pH value and current density, and the pH value and current density are mainly concerned. The corrosion resistance of Ni-W alloy coating is excellent compared with that of Cr and Ni coatings.
The electro-deposition method was used for preparation of nanocrystalline Ni-W alloys coating. The formation, microstructure and performance of the nanocrystalline were investigated. X-ray diffraction results show that Ni-W alloys are crystallized in scale of 1730nm. Changing with the depositional time, the coating varies with different surface morphology. The observation on the formation of the coating implies that, the alloys preferentially deposit and grow on the scratch and corrosion pit edges. The hardness of the alloy coatings is related to the solution composition, pH value and current density, and the pH value and current density are mainly concerned. The corrosion resistance of Ni-W alloy coating is excellent compared with that of Cr and Ni coatings.
出处
《中国有色金属学会会刊：英文版》
CSCD
2005年第S3期198-202,共5页
Transactions of Nonferrous Metals Society of China
基金
Project(05022047)supportedby2005AnnualScientificProgramofAnhuiProvince
project(00046403)supportedbytheNaturalScienceFoundationofAnhuiProvince