摘要
Self-organized TiO2 nanotubes were prepared on titanium foils at anodizing voltage of 20V in 0.5% HF solution for 2030min in order to provide a novel high-efficiency photocatalyst. And the resulting TiO2 nanotubes, in periodic ring structures around their exteriors, are open on the top, while closed on the bottom. After annealing for 3h in ambient atmosphere, the anatase phase was found, with the increasing content, in the originally amorphous TiO2 nanotubes treated at 350, 400 and 450℃; whereas the rutile phase emerged at 500℃, and the nanotube architecture could be preserved till 550℃. Furthermore, TiO2 nanotubes, fabricated at anodizing voltage of 20V for 20min and then annealed at 400℃, possesses the best photo-catalytic activity, i.e. the decolourisation of methyl orange irradiated for 40min is 99.6%.
Self-organized TiO_2 nanotubes were prepared on titanium foils at anodizing voltage of 20V in 0.5% HF solution for 2030min in order to provide a novel high-efficiency photocatalyst. And the resulting TiO_2 nanotubes, in periodic ring structures around their exteriors, are open on the top, while closed on the bottom. After annealing for 3h in ambient atmosphere, the anatase phase was found, with the increasing content, in the originally amorphous TiO_2 nanotubes treated at 350, 400 and 450℃; whereas the rutile phase emerged at 500℃, and the nanotube architecture could be preserved till 550℃. Furthermore, TiO_2 nanotubes, fabricated at anodizing voltage of 20V for 20min and then annealed at 400℃, possesses the best photo-catalytic activity, i.e. the decolourisation of methyl orange irradiated for 40min is 99.6%.
出处
《中国有色金属学会会刊：英文版》
CSCD
2005年第S3期462-466,共5页
Transactions of Nonferrous Metals Society of China
基金
Project(BK2004129)supportedbytheNaturalScienceFoundationofJiangsuProvince,China
Project(04H52059)supportedbytheAeronauticScienceFoundation,China